Hi Steve,
The fact that it lifted in the first palce is not comforting but it appears
to be on the coverlayer/coverfilm only so you might be ok. Tears once
initiated, tend to propagate. Chuck's suggestion should work. Another approach would
be to try can get the tear to turn back to the edge and then coat it with a
thin coat of silicon RTV or flexible epoxy. As long as it does not get abused
you should be Ok.
Good luck,
Joe
************************************** See what's free at http://www.aol.com.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------