Steve and James, congratulations on your engagement!
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Inge
Sent: Thursday, March 22, 2007 12:56 PM
To: [log in to unmask]
Subject: Re: [TN] AlSiC conclusion
Steve,
hey down there, do you here me? You needn't dig any more, I have got
answer on my question. As you and James said, it's very simple. You buy
the matrix with pure aluminum skin, and then plate like for ordinary Al
sheets. The matrix with non-skin is treated with thermal spray (Copper
plasma) as I said, not of interest for us. So, thanks for your
engagement, both of you.
Inge
----- Original Message -----
From: "Creswick, Steven" <[log in to unmask]>
To: <[log in to unmask]>
Sent: Thursday, March 22, 2007 1:20 PM
Subject: Re: [TN] AlSiC
Ingemar,
I am still going to have to do more digging. I could have sworn that it
was either PCC Composites or Lanxide Electronic Components that inserted
the pre-compressed slug into the mold then infiltrated around it - but a
quick look on their sites did not reveal it to me. Possibly my info is
out of date and they dropped this.
This is what I have for now, but will look further. Have files at home
that moved with me that will take some digging to find the pearls I am
searching for. Will scrounge through them this weekend.
Lanxide Electronic Components
http://www.patentstorm.us/patents/5526867.html
PCC-Advanced Forming Technology
http://www.matweb.com/search/SpecificMaterialText.asp?bassnum=NZMPC0
http://www.pcc-aft.com/
http://www.mmmt.com/Profile.html
http://www.mc21inc.com/
Regarding flight time/fuel capacity. I can carry up to 14 gal US [53L].
Fuel consumption rate is 2-2.5 Gal/hr [7.5-9.5L/hr]. Airspeed is 30
miles per hour [48 km/hr], so if I have a 10 mph tailwind, by ground
speed is a whopping 40 mph [68 km/h]! Powered parachutes are not for
long distance flights. Low and slow!
Legally we can go up to 10,000 ft, but I have not gone above 3500 ft -
imagine being strapped into your kitchen chair, in the open, at 10,000
ft! Not sure even I am ready for that. My radar cross-section is
small. See no need to be up where the 'big boy' commercial aviation
aircraft are!
At 200-2000 ft, ones gets an entirely new appreciation for the sights
and smells of the earth below.
You should visit your local flight park and hitch a ride. Wear warm
clothes and bring a camera with good strap on it. Also have someone on
the ground take a picture after you land - showing the look of wonder
.....or terror [sorry, could not resist] :-)
I know of a local flight instructor that took up an 80 year old
gentlemen a year or so back. The guy just loved it!! My wife even
likes to go up with me, and she does not like heights! She will not
climb a step ladder more than about a meter or so. One is strapped in
quite well, so you get the feeling of being part of the machine -
especially in the back seat - which is what allows her to overcome her
fears. She immensely enjoys the view, but not cold temperatures.
The chute is already deployed. Power-lines are our worst enemy.
Steve
-----Original Message-----
From: Hernefjord Ingemar [mailto:[log in to unmask]]
Sent: Thursday, March 22, 2007 3:05 AM
To: TechNet E-Mail Forum; Creswick, Steven
Subject: RE: [TN] AlSiC
Yes, please, if not taking too much of your flight time.
(Thanks for trike pictures. What if Leonardo had seen that? "YES! YES! I
knew it would work! " There is a small club nearby, just about 10
members, I hear them long before they appear in the sky. Sounds like
midgets. How far can you go on normal fuel tank?)
Inge
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Creswick, Steven
Sent: den 21 mars 2007 12:16
To: [log in to unmask]
Subject: Re: [TN] AlSiC
Ingemar,
It would seem that the SiC matrix should have been fully infiltrated
with the molten Al. Maybe you did not expect the blisters to be from
gas entrapment... What do you believe the source of the blistering to
be?
There was a time when someone was taking the AlSiC 'slug' and placing
that inside an aluminum casting - which could later be milled down, but
still leaving aluminum over the AlSiC slug.
From there plating was a snap.
Want me to dig out who it was that did it?
Steve
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Inge
Sent: Tuesday, March 20, 2007 3:39 PM
To: [log in to unmask]
Subject: [TN] AlSiC
Honoured Messieurs wet chemists,
have to make solderable finish on AlSiC substrates. Got copper plated
samples from manufacturer. We did usual 300 Centigrade blister test, and
as expected, large blisters were created. Now, what suitable finish do
you recommend? Would like to try nickel sputter+electrolytic nickel+gold
flash, but there may be wet chemistry for the adhesion layer instead of
sputtering or thermal spray. There are tin plating methods too, but
they seem not to be for soldering , but rather act as environment
protection coatings.
Inge
-----------------------------------------------------
THE INFORMATION CONTAINED IN THIS E-MAIL MESSAGE AND ANY ATTACHMENTS
SENT FROM GENTEX CORPORATION IS GENTEX CONFIDENTIAL INFORMATION INTENDED
ONLY FOR THE PERSONAL USE OF THE INDIVIDUAL OR ENTITY NAMED ABOVE. If
you are not the intended recipient, you are hereby notified that any
review, distribution, or copying of this communication is strictly
prohibited. If you have received this communication in error, please
immediately notify the sender by return e-mail, and delete this e-mail
message and any attachments from your computer.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
THE INFORMATION CONTAINED IN THIS E-MAIL MESSAGE AND ANY ATTACHMENTS
SENT
FROM GENTEX CORPORATION IS GENTEX CONFIDENTIAL INFORMATION INTENDED ONLY
FOR
THE PERSONAL USE OF THE INDIVIDUAL OR ENTITY NAMED ABOVE. If you are not
the
intended recipient, you are hereby notified that any review,
distribution,
or copying of this communication is strictly prohibited. If you have
received this communication in error, please immediately notify the
sender
by return e-mail, and delete this e-mail message and any attachments
from
your computer.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|