Rodney Miller <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Rodney Miller <[log in to unmask]>
Date:
Fri, 23 Feb 2007 14:58:23 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (37 lines)
Dear Technetters,
 
Is XRF the best way to evaluate the condition of BGA packaging prior to
reflow?
 
I have an ALI chip which has gone EOL.  The customer is "testing" them,
but my yields are poor after reflow.  Due to the age and source of the
components, I suspect there may be damage to the Packaging and I'd like
to verify this prior to processing them.  
 
Whaddaya think?  
 
Is there a good way to review moisture content or damage to the
components.  Xray seems limited in its discrete ability to give me
condition of "softtissue" damage.   Anybody ever check weight before and
after baking or would inherent error be to great to reveal anything of
substance?
 
I look forward to your input,
 
Rodney L. Miller
Tri-onics Inc
Highland / Shanghai
 
Integrity and Solutions for Electronic Outsourcing
 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2