Subject:
From:
"Dehoyos, Ramon" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Dehoyos, Ramon
Date:
Fri, 2 Feb 2007 08:41:49 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (181 lines)
	The pin seems to be intact. The solder joint appears to have
caved in and separated from the pin. Something needs to be changed.
Either just tack two pins to hold the Converter prior to have the heat
sink attached, then reflow both pins at the same time and finish
soldering the rest of the pins manually or change the way the heat sink
is attached so that it does not pull the converter during attachment.
	Ramon
 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Wayne Thayer
Sent: Thursday, February 01, 2007 4:35 PM
To: [log in to unmask]
Subject: Re: [TN] Mechanical Stress on solder joints

Gary-

The bottom line is that electrical solder is not a reasonable load
bearing material.  You can relieve the stress in the joints by reflowing
the connections after attaching the heatsink.  IF the pins aren't long
enough to make that work, then re-think your mounting, because there is
no way that it will be reliable with the joints under stress, even if
there is no additional environmental stress placed on the system.

Wayne Thayer

>>> [log in to unmask] 2/1/2007 3:51:03 pm >>>
Steve,

This is side view of the module with the broken pin. There is a heatsink
above approximately 0.100 thick with 4 screws pulling the DC/DC
converter upward away from the circuit board. I do not want to place any
solder joints under load wither it be clamping or pulling forces. 

Thanks,

Gary Bremer
Senior Manufacturing Engineer, CIT
Phone: 257-4430 extension 2170


-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Steve Gregory
Sent: Thursday, February 01, 2007 9:35 AM
To: [log in to unmask]
Subject: Re: [TN] Mechanical Stress on solder joints

Hi Gary!

I have your picture posted. It's at:
http://stevezeva.homestead.com/files/Broken_Pin.jpg 

It sure looks like something has pulled or stressed that pin. I'm trying
to visualize the heatsink, but I can't form a mental picture of it, so I
can't say for sure if it was the heatsink or not. But from your
description, it seems pretty probable that the stress that you describe
damaged that pin.

-Steve Gregory-

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bremer, Gary
Sent: Thursday, February 01, 2007 10:02 AM
To: [log in to unmask]
Subject: [TN] Mechanical Stress on solder joints

Gentlemen,

 

I have a device that failed in the field, the part is a DC/DC converter
that is first soldered to the circuit board then a massive heatsink is
screwed to the converter pulling the device upward because of an air gap
not covered by a thermal conductive pad. Could this be the cause of
damage to the component pins as shown in the attached photo? The solder
used is Sn63 on the circuit board side and the mass of the board solder
joint appears to be twice that of the component.

 

Gary Bremer
Senior Manufacturing Engineer, CIT
  
Curtiss-Wright Controls Inc. 
Embedded Computing -Subsystem

28965 Avenue Penn
Santa Clarita, CA 91355-4185
Main: 661.257.4430 extension 2170
Fax: 661.257.4782


e-mail: [log in to unmask]
Web: www.cwcembedded.com 

NOTICE: This e-mail communication is private and confidential and is
intended for the addressee only. The email may only be used for
conducting business with VISTA Controls Inc., dba Curtiss-Wright
Controls Embedded Computing Subsystems. If you are not the intended
recipient, please notify us by replying to this email followed by
deleting the email and all attachments from your system. Anyone other
than the intended recipient or those with a need to know within the
recipient's organization is strictly prohibited from using, printing,
distributing or disseminating the email or any information or attachment
contained therein.

 


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

______________________________________________________________________
 <<Failed Module.bmp>>  <<heatsink.jpg>> 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2