Richard Kraszewski:
The non-lead (thus high Tin) solders could give you some interesting challenges in cleaning/descaling, which previous cleaners may not be up to handling. We have seen some evidence of this, and have created some answers that handle normal water hardness deposits, as well as the Tin oxide deposits.
Rudy Sedlak
RD Chemical Company
Richard Kraszewski <[log in to unmask]> wrote: Argh , yes!!! Great idea! My only hesitation are those whinny & pesky
humanoid operators we have populating the factory complaining about the
odors. Hoping to find something a wee bit more agreeable with them.
Rich K / GTS
847-621-7310
-----Original Message-----
From: Dee Stover [mailto:[log in to unmask]]
Sent: Tuesday, January 09, 2007 12:52 PM
To: TechNet E-Mail Forum; Richard Kraszewski
Subject: Re: [TN] Descaling of Water Wash Systems
Something I use at home is white vinegar - tea Kettle and humidifier
10 min or less, soak, then rinse.
At 10:23 AM 1/9/2007, you wrote:
>To ~continue along this forum's recent cleaning track...
>
>What are you using for de-scaling water wash systems?
>
>Any recommendations would be appreciated.
>
>Rich K / GTS
>
>
>---------------------------------------------------
>Technet Mail List provided as a service by IPC using LISTSERV 1.8e
>To unsubscribe, send a message to [log in to unmask] with following text
in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of Technet send e-mail to
>[log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts: send e-mail to
>[log in to unmask]: SET Technet Digest
>Search the archives of previous posts at:
http://listserv.ipc.org/archives
>Please visit IPC web site
>http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
>information, or contact Keach Sasamori at [log in to unmask] or
>847-615-7100 ext.2815
>-----------------------------------------------------
:-) Dee Stover [log in to unmask]
Tech Associate II
National Optical Astronomy Observatories
www.noao.edu
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
__________________________________________________
Do You Yahoo!?
Tired of spam? Yahoo! Mail has the best spam protection around
http://mail.yahoo.com
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|