Thank you for posting these articles, Gabriela.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Gabriela Bogdan
Sent: Tuesday, December 12, 2006 9:51 AM
To: [log in to unmask]
Subject: Re: [TN] 58Bi/42Sn /// HASL for PCBs
Well, if you want to play an "Uri Geller" trick to your customers, maybe
it is a good idea...
Here they are soldered- and now: Abrakadabra- they all fall off just by
my magic touch!
Gaby
http://www.mse.uiuc.edu/faculty/Shang/Preprints/1997-2006/ScriptaBi.pdf
http://www.mrs.org/s_mrs/bin.asp?CID=2274&DID=48689&DOC=FILE.PDF
----- Original Message -----
From: "Reuven Rokah" <[log in to unmask]>
To: <[log in to unmask]>
Sent: Tuesday, December 12, 2006 9:54 AM
Subject: Re: [TN] 58Bi/42Sn /// HASL for PCBs
> I think its can be good alloy for PCBs HASL plating.
>
> If someone against, pls explain why not.
>
> Best Regards
> Reuven ROKAH
> e mail: [log in to unmask]
>
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of David D. Hillman
> Sent: Tuesday, December 12, 2006 1:34 AM
> To: [log in to unmask]
> Subject: Re: [TN] 58Bi/42Sn
>
> Hi Kerry - Dr. Hwang's book titled "Environment Friendly Electronics:
> Lead-free Technology", ISBN 0-901150-40-1, Chapter 6.2, contains a
> significant amount of data on the 58Bi/42Sn solder alloy which may be
> helpful in your efforts. Good Luck.
>
> Dave Hillman
> Rockwell Collins
> [log in to unmask]
>
>
>
>
> Kerry McMullen
> <Kerry_McMullen@L
> TX.COM>
> To
> Sent by: TechNet [log in to unmask]
> <[log in to unmask]>
> cc
>
>
> Subject
> 12/11/2006 09:01 [TN] 58Bi/42Sn
> AM
>
>
> Please respond to
> TechNet E-Mail
> Forum
> <[log in to unmask]>
> ; Please respond
> to
> Kerry_McMullen@LT
> X.COM
>
>
>
>
>
>
> Hello esteemed Technet,
> I am looking comments on what you would consider the advantages
> and disadvantages of this composition of this solder paste.
> (58Bi/42Sn) Lower MP. 138 Degrees C.
> Lower fatigue resistance
> Wetting to ImAg??
> Wetting to ImNiAu??
> No Clean? Residue?
> Intermetallic Formation?
> Mixing with 63/37Sn?
> Our application is an RF board where we would use this paste post Wave
> / Hand Solder.
> Any comments appreciated.
>
> Cheers,
> Kerry
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
> unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt
> or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
> per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
> http://listserv.ipc.org/archives
> Please visit IPC web site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at
> [log in to unmask] or 847-615-7100 ext.2815
> -----------------------------------------------------
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
> unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt
> or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
> per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
> http://listserv.ipc.org/archives
> Please visit IPC web site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
> information, or contact Keach Sasamori at [log in to unmask] or
> 847-615-7100
> ext.2815
> -----------------------------------------------------
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
> unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt
> or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
> per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
> http://listserv.ipc.org/archives Please visit IPC web site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at
> [log in to unmask] or 847-615-7100 ext.2815
> -----------------------------------------------------
>
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|