Hi Ioan,
You write:
> "Time above liquidous is 65s."--I think you mean Solidus.
> Did you not take my workshop? Time above Solidus is a meaningless parameter;
for assured reflow you need 3 to 5 seconds at Liquidus + 20C if soldering to
Cu, more if soldering to Ni.
Werner
---------------------------------------------------