Probably a lower melting point.
Blair
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of arnaud grivon
Sent: Friday, September 22, 2006 9:20 AM
To: [log in to unmask]
Subject: Re: [TN] Soldering with Sn9,5Ag3,5
Could anybody on the TechNet planet tell me the primarily reasons for using this Sn96,5Ag3,5 solder alloy?
It looks like this alloy has been already in use for some years as solder wires and solder paste for small electronic modules.
Also, I seem to remind that this was the first alloy of choice for lead-free BGA spheres before the industry consensus for SAC.
Why did the industry switch to SAC instead of SnAg? In other words, what does the copper bring?
A. Grivon
Juan T. Marugán a écrit :
> Hi,
>
> in a Class 3 product (aerospace) we have to solder some wires to a PCB
> using a Sn96,5Ag3,5 solder alloy. Wires are silver coated,
> high-strength copper alloy and the PCB is SnPb plated.
>
> My first question is, Do you consider that solder alloy as a good option?
>
> Besides, in a near future, we will change the finish of the PCB from
> SnPb to ENIG. In that situation, what solder alloy do you recommend us?
>
> Thank you in advance.
>
> Juan T. Marugán
> Production QA
> Indra Sistemas SA
> Spain
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
> unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt
> or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET
> Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
> posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
> archives of previous posts at: http://listserv.ipc.org/archives Please
> visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at
> [log in to unmask] or 847-615-7100 ext.2815
> -----------------------------------------------------
>
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
*******************************************************************
This email and any files transmitted with it are confidential and
intended solely for the use of the individual or entity to whom they
are addressed. If you have received this email in error please notify
the system manager.
This footnote also confirms that this email message has been swept
for the presence of computer viruses.
www.hubbell.com - Hubbell Incorporated
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|