Dear Technetter
As you know that excessive copper rate in both Sn/Pb and SAC305 may 
cause soldering problem on assembly side. For eutectic Sn/Pb solder for 
ex 63/37 copper rate should  not be more than 0.25 %. We could smear 
excess copper on molten solder. We heat up the solder up to 240-250 C 
and then strat to cool it down to 183 C which is the temperature of 
copper melting point, other alloys settle down and copper gathers on the 
surface and we smear it. This is one of the reducinmg copper rate for 
63/37 Sn/Pb solder.
During the HAL process when soldering process is continuing copper rate 
increase gradually so we need to decrease copper rate. In this view, we 
want to learn that if there is any method to reduce the excessive copper 
in SAC305, do you have any experinece aor have you heard of any method 
to reduce copper inside SAC305

Best Regards

-- 
Yusuf GÖMEÇ
Process Engineer


BASKI DEVRE SAN ve TIC LTD STI
Ceyhan Sk. No:10 34896 Pendik-Istanbul-Turkey
Tel: 00 90 216 3901036 (4 Hat/Line)-173(Extention)
     00 90 216 4836560 (4 Hat/Line)-173(Extention)
Fax: 00 90 216 3544941
     00 90 216 4913269
Gsm: 00 90 533 6579897
     00 90 533 7480014 
msn: [log in to unmask]

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------