"the hole truth"
                Platitudes 50:260
Dewey
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Werner Engelmaier
Sent: Wednesday, August 02, 2006 3:23 PM
To: [log in to unmask]
Subject: Re: [TN] Barrel to Laminate Adhesion loss

Hi Richard & All,
Actually, the higher occurrances of hole wall separation and trace
separation 
are not so much caused by more lateral stresses, but the different
thermal 
and mechanical properties of SAC solders.
To understand what is happening, one really needs to understand what the

whole damage process causing hole wall separation [sometimes also called
resin 
recession] and inner-layer separation [also called post separation or
trace 
separation.
(1) On heating the resin expands-because of the glass fiber
reinforcement it 
is prevented to expand in x/y and thus expands in z at nearly 3-times
its 
thermal expansion without the glass reinforcement]; there is an
exception to this-
the resin also tries to expand into the volume occupied by the PTH, and
is of 
course, to some degree at least, prevented from doing so by the Cu
barrel 
plating. 
Thin Cu plating and/or large separation between inner-layer land
[serving as 
anchors] encourage larger bulging inwards of the Cu with plastic
deformation 
of the Cu.
(2) On cooling, the resin contracts to its former volume-if the Cu is 
plastically deformed to a significant degree, it cannot do so: the
result=>hole wall 
separation, and near the surface in connection with land rotation
inner-layer 
separation.
(3) For SnPb solders the Solidus is 183C; thus, Solidus - Tg
(183-170C)~13C.
For SAC solders the solidus is 217C; thus, Solidus - Tg (217-170C)~47C.
The consequence is that the delta-T after solder solidification is about

4-times larger for SAC-solders, over which the high above Tg-thermal
contraction 
acts-and this also holds the Cu back to its former position: the result
=>more 
hole wall separation, and inner-layer separation.

Pretty straight-forward when you think about.

Werner

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------