TECHNET Archives

June 2006

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
"Bloomquist, Ken" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Bloomquist, Ken
Date:
Wed, 21 Jun 2006 09:30:19 -0700
Content-Type:
text/plain
Parts/Attachments:
text/plain (54 lines)
Oh No, it's De ja-dewey in the middle of the week ;-)

Thanks, Mike!

-----Original Message-----
From: Barmuta, Mike [mailto:[log in to unmask]] 
Sent: Wednesday, June 21, 2006 9:26 AM
To: TechNet E-Mail Forum; Bloomquist, Ken
Subject: RE: [TN] Conformal Coat Voids

Hi Ken: Maybe it is outgassing of organics from the tin....

Sorry Ken I couldn't help myself. 


                                                        Regards
	
Mike B.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Bloomquist, Ken
Sent: Wednesday, June 21, 2006 9:16 AM
To: [log in to unmask]
Subject: [TN] Conformal Coat Voids

We are seeing something that we've never noticed before and wondering if
any of you have seen it and figured out a cure.

We are hand spray Type UR coating. The boards are very well cleaned and
dried prior to coating. What we are seeing is a lack of coating on top
of via's. It's most prevalent on small via's, .013" but we're seeing it
on some of the larger ones as well. When we black light the board you
can see black spots on top of the solder in the via.

It's not just a thin coating but an actual void area. It's exactly on
the dome of the solder of the via. Our nominal coating thickness is
around .003".

I sure would appreciate any help on finding a cure for this!

Thanks,

KennyB

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2