Two experiences were shared with me and would like them to be
known for comments. In one instance a COTS BGA was used on a prototype.
It would not wet to SN63Pb37 after several attempts and profile
temperature increments It was found out that it had SAC 305 balls. Has
anyone experienced that SAC does not wet well with eutectic tin lead
solder paste? In another instance balls from SAC and Tin Lead were found
in the same BGA. Apparently solder balls were inadvertently mixed.
Ramon
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------