Badri
If the component will see more than 220 DegC for around 2 to 3
seconds - yes, but you might want to check out the joint integrity...
Kindest regards
Graham Naisbitt
[log in to unmask]
Phone: +44 (0)12 5252 1500
Mobile: +44 (0) 79 6858 2121
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
Unit B2, Armstrong Mall
Southwood Business Park
Farnborough Hampshire
GU14 0NR - UK
ENGINEERING RELIABILITY
IN ELECTRONICS
DISCLAIMER : This message is intended only for the use of the
individual or entity to which it is addressed and may contain
information which is privileged, confidential, proprietary, or exempt
from disclosure under applicable law. If you are not the intended
recipient or the person responsible for delivering the message to the
intended recipient, you are strictly prohibited from disclosing,
distributing, copying, or in any way using this message. If you have
received this communication in error, please notify the sender and
destroy and delete any copies you may have received. Any views or
opinions presented in this email are solely those of the author and
might not represent those of Gen3 Systems Limited. Although Gen3
Systems Limited has taken reasonable precautions to ensure no viruses
present in this email, Gen3 Systems Limited can not accept the
responsibility for any loss or damage arising from the use of this
email or attachments.
On 22 Jun 2006, at 12:22, Badri wrote:
> Hello All,
>
> Can I reflow solder a lead free component (chip components)in the
> leaded
> process/profile. Will there be any solderability issue. Advenace
> thanks for
> the help you are rendering.
>
> Thanx
> Badri
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following
> text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail
> to [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/
> archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?
> Pageid=4.3.16 for additional information, or contact Keach Sasamori
> at [log in to unmask] or 847-615-7100 ext.2815
> -----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|