Subject:
From:
- Bogert <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, - Bogert <[log in to unmask]>
Date:
Thu, 2 Mar 2006 18:58:11 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (134 lines)
March 2, 2006

Thanks.  I did realize Technet strips attachments.  I tried embedding them directly within the e-mail.  They did not lake that either so I forwared the attached photos to Steve.
  ----- Original Message ----- 
  From: Stadem, Richard D.<mailto:[log in to unmask]> 
  To: [log in to unmask]<mailto:[log in to unmask]> 
  Sent: Thursday, March 02, 2006 8:28 AM
  Subject: Re: [TN] Black "crud" on connector solder connections causing electrical short-circuit - Need Help Please


  Bogert, 
  All attachments are stripped off on Technet postings. Perhaps Steve
  Gregory can post them on his website. Else if you can provide a link to
  a Net site... 

  -----Original Message-----
  From: TechNet [mailto:[log in to unmask]] On Behalf Of Richard Kraszewski
  Sent: Wednesday, March 01, 2006 8:01 PM
  To: [log in to unmask]<mailto:[log in to unmask]>
  Subject: Re: [TN] Black "crud" on connector solder connections causing
  electrical short-circuit - Need Help Please

  I don't see any photos.

  Rich K / KEDS
  260.925.8719
   
  -----Original Message-----
  From: TechNet [mailto:[log in to unmask]] On Behalf Of - Bogert
  Sent: Wednesday, March 01, 2006 6:51 PM
  To: [log in to unmask]<mailto:[log in to unmask]>
  Subject: [TN] Black "crud" on connector solder connections causing
  electrical short-circuit - Need Help Please

  March 1, 2006

  Folks, the three attached photographs show some problems an OEM of ours
  is having.  Specifically, he hand solders two MIL-W-16878 silver coated
  stranded wires to a MIL SPEC connector that has solder eyelets plated
  with 50 microinch of gold.  Sn10 WRMAP flux cored solder is used with no
  additional flux added.  The OEM has had recent rash of failures in
  fielded equipment.  We do not know the cause yet.  We are having the
  black residue shown sent out for analysis but no results yet.

  The solder joints do not appear to be acceptable to me.  One can see
  exposed gold on the gold-plated connector contact eyelets.  Appears to
  be non-wetting???  Also, appears to be excess solder since strands are
  not always visible in the joint.  The OEM tins the stranded wire with
  Sn63 prior to soldering.

  Do you folks have any ideas on what the problem could be?  There is
  detailed info on the photographs on the application of the product.  The
  connector provides power to a solenoid that actuates a valve.  

  The application is hermetic sealed by welding the connector to a metal
  housing that contains the solenoid winding.  The wires connecting to the
  connector are the MIL-W-16878 silver coated stranded lead wires that
  connect from the gold plated connector pins on one end to the MIL SPEC
  magnet wires on the solenoid on the other end.  The solenoid is
  varnished (DIP process, no vacuum).  

  I am aware that silver plated wire in an SO2 environment can cause
  corrosion, but we use a lot of silver coated wire in other product with
  no known corrosion problems.

  The connector housing has a small vent port into which air is applied to
  do a pressure seal test.  After the pressure test is completed, the vent
  hole plug is welded closed.  We are checking to see if the air could
  have had moisture in it.

  Dielectric strength, insulation resistance and functional testing is
  done on the solenoid after assembly is completed and all tests passed.
  However, failures occur in the field.

  Since the flux used in the SN10 flux-cored solder is RMA, one would
  normally not expect the black residue to be due to RMA flux but I am not
  sure.  We will probably know for certain after we get the test results
  on the black crud.

  Any insight you may have into into this problem would be appreciated.

  Please e-mail your response to following e-mail address:

  [log in to unmask]<mailto:[log in to unmask]<mailto:[log in to unmask]<mailto:[log in to unmask]>>

  ---------------------------------------------------
  Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
  unsubscribe, send a message to [log in to unmask]<mailto:[log in to unmask]> with following text in
  the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
  (re-start) delivery of Technet send e-mail to
  [log in to unmask]<mailto:[log in to unmask]>: SET Technet NOMAIL or (MAIL) To receive ONE mailing
  per day of all the posts: send e-mail to
  [log in to unmask]<mailto:[log in to unmask]>: SET Technet Digest
  Search the archives of previous posts at:
  http://listserv.ipc.org/archives<http://listserv.ipc.org/archives>
  Please visit IPC web site
  http://www.ipc.org/contentpage.asp?Pageid=4.3.16<http://www.ipc.org/contentpage.asp?Pageid=4.3.16> for additional
  information, or contact Keach Sasamori at [log in to unmask]<mailto:[log in to unmask]> or 847-615-7100
  ext.2815
  -----------------------------------------------------

  ---------------------------------------------------
  Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
  unsubscribe, send a message to [log in to unmask]<mailto:[log in to unmask]> with following text in
  the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
  (re-start) delivery of Technet send e-mail to [log in to unmask]<mailto:[log in to unmask]>: SET
  Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
  posts: send e-mail to [log in to unmask]<mailto:[log in to unmask]>: SET Technet Digest Search the
  archives of previous posts at: http://listserv.ipc.org/archives<http://listserv.ipc.org/archives> Please
  visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16<http://www.ipc.org/contentpage.asp?Pageid=4.3.16> for
  additional information, or contact Keach Sasamori at [log in to unmask]<mailto:[log in to unmask]> or
  847-615-7100 ext.2815
  -----------------------------------------------------

  ---------------------------------------------------
  Technet Mail List provided as a service by IPC using LISTSERV 1.8e
  To unsubscribe, send a message to [log in to unmask]<mailto:[log in to unmask]> with following text in
  the BODY (NOT the subject field): SIGNOFF Technet
  To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]<mailto:[log in to unmask]>: SET Technet NOMAIL or (MAIL)
  To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]<mailto:[log in to unmask]>: SET Technet Digest
  Search the archives of previous posts at: http://listserv.ipc.org/archives<http://listserv.ipc.org/archives>
  Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16<http://www.ipc.org/contentpage.asp?Pageid=4.3.16> for additional information, or contact Keach Sasamori at [log in to unmask]<mailto:[log in to unmask]> or 847-615-7100 ext.2815
  -----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2