TECHNET Archives

January 2006

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
Ted Tontis <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Ted Tontis <[log in to unmask]>
Date:
Mon, 30 Jan 2006 15:44:51 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (32 lines)
Jon,
        If your product is not class three and you are getting at least
180 degrees on the solder side 75% vertical fillet 270 degrees on the
secondary side (270 degrees around the lead) and 75% of solder on the
pad on the secondary side you should be fine.	

        If you require class three then it would be 270 degrees on the
solder side, 75% vertical fillet, 330 degrees on the secondary side (330
degrees around the lead) and 75% of solder on the pad on the secondary
side.

        That's from A-610 Rev C. 

        If you are still not getting the flow you want try adjusting the
speed of the wave. Lead free solder doesn't flow well so slowing down
the wave and allowing the solder time to wick, will increase the volume
of solder on the primary side of the PCB. 

Good luck,

Ted

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2