-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Whittaker, Dewey
(AZ75)
Sent: Friday, January 20, 2006 5:51 AM
To: [log in to unmask]
Subject: Re: [TN] Soldering matte tin over nickel plating NTC
That's OK Dave, some people still think I'm one of Donald's nephews. How
Daffy is that. Besides you and Doug will probably here it from John
Burke, who has been apparently filling in for me while I was away.
Besides I wouldn't want to say anything because it's your turn to buy in
Anaheim and your were right about sending the PWBs back.
Dewey
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of David D. Hillman
Sent: Thursday, January 19, 2006 4:13 PM
To: [log in to unmask]
Subject: Re: [TN] Soldering matte tin over nickel plating NTC
Pay no attention to Doug - he is just playing the role of Goofy today -
one of our school educational "shows" experiments didn't work the first
time he gave it a try! (was Goofy one of the 7 dwarfs? if not then I am
in big trouble).
Dave Hillman
Rockwell Collins
"Douglas O.
Pauls"
<dopauls@ROCKWELL
To
COLLINS.COM> [log in to unmask]
Sent by: TechNet
cc
<[log in to unmask]>
Subject
Re: [TN] Soldering matte tin over
01/19/2006 05:01 nickel plating
PM
Please respond to
TechNet E-Mail
Forum
<[log in to unmask]>
; Please respond
to
dopauls@ROCKWELLC
OLLINS.COM
Yes, I am happy to report the SnO2 White consideration dwarfs the
others, however Grumpy that makes people.
Beetcha to it Dewey
Doug Pauls
Leo Higgins
<Leo_Higgins@ASAT
.COM>
To
Sent by: TechNet [log in to unmask]
<[log in to unmask]>
cc
Subject
01/19/2006 04:45 Re: [TN] Soldering matte tin over
PM nickel plating
Please respond to
TechNet E-Mail
Forum
<[log in to unmask]>
; Please respond
to
Leo Higgins
<Leo_Higgins@ASAT
.COM>
Agree with Dave. Matte tin should look dull silver-gray. SnO2 is
white.
I
have seen matte tin get quite white if the parts have been stored a
"long"
time allowing the units to get oxidized.
Best regards,
Leo
Leo M. Higgins III, Ph.D.
Vice President, Technical Support Operations ASAT, Inc.
3755 Capital of Texas Highway, Suite 100
Austin, Texas 78704
office phone 512-383-4593
mobile 512-423-2002
[log in to unmask]
www.asat.com
The information contained in this electronic message is
CUSTOMER/SUPPLIER PRIVILEGED AND CONFIDENTIAL INFORMATION intended only
for the use of the individual or entity named above. If the reader of
this message is not the intended recipient, you are hereby notified that
any dissemination, distribution and copying of this communication is
strictly prohibited. If you have received this communication in error,
please immediately notify the sender by electronic mail. Thank you.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of David D. Hillman
Sent: Thursday, January 19, 2006 4:30 PM
To: [log in to unmask]
Subject: Re: [TN] Soldering matte tin over nickel plating
Hi John! A white deposit on a matte tin finish can not be a good thing
and is not normal for the matte tin finishes I am familiar with. I would
subject the components to the JSTD-002B Test S (Surface Mount Simulation
test) to see if it passes. If it fails then you have leverage with your
vendor based on data and not observation. Good Luck.
Dave Hillman
Rockwell Collins
[log in to unmask]
John Burris
<johnhburris@GMAI
L.COM>
To
Sent by: TechNet [log in to unmask]
<[log in to unmask]>
cc
Subject
01/19/2006 08:54 [TN] Soldering matte tin over
AM nickel plating
Please respond to
TechNet E-Mail
Forum
<[log in to unmask]>
; Please respond
to
John Burris
<johnhburris@GMAI
L.COM>
Dear TechNetters,
We are just starting our journey into lead-free (we are currently
covered under Article 9, but we can see the handwriting on the wall),
and we are starting to deal with some issues as suppliers are making
component changes to comply with RoHS. The component at issue is a heat
sink for a TO-220 transistor. Flux is 2% no-clean. Solderability is not
good; partial solder adhesion (about 20-30%) on the mounting tabs. 90%
coverage is required by standards. The matte tin finish appears to have
a white deposit that can be removed by either scraping or cleaning with
a mild solvent. Vendor says this is normal and should not affect
solderability.
Thoughts?
John Burris
Automated Logic
1150 Roberts Blvd.
Kennesaw, GA 30144-3618
01.770.795.4827 (Office)
01.770.795.3527 (Facimile)
01.404.431.9109 (Cellular)
--
No virus found in this outgoing message.
Checked by AVG Free Edition.
Version: 7.1.375 / Virus Database: 267.14.20/233 - Release Date:
1/18/2006
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing
per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|