Yes, I am happy to report the SnO2 White consideration dwarfs the others,
however Grumpy that makes people.
Beetcha to it Dewey
Doug Pauls
Leo Higgins
<Leo_Higgins@ASAT
.COM> To
Sent by: TechNet [log in to unmask]
<[log in to unmask]> cc
Subject
01/19/2006 04:45 Re: [TN] Soldering matte tin over
PM nickel plating
Please respond to
TechNet E-Mail
Forum
<[log in to unmask]>
; Please respond
to
Leo Higgins
<Leo_Higgins@ASAT
.COM>
Agree with Dave. Matte tin should look dull silver-gray. SnO2 is white.
I
have seen matte tin get quite white if the parts have been stored a "long"
time allowing the units to get oxidized.
Best regards,
Leo
Leo M. Higgins III, Ph.D.
Vice President, Technical Support Operations
ASAT, Inc.
3755 Capital of Texas Highway, Suite 100
Austin, Texas 78704
office phone 512-383-4593
mobile 512-423-2002
[log in to unmask]
www.asat.com
The information contained in this electronic message is CUSTOMER/SUPPLIER
PRIVILEGED AND CONFIDENTIAL INFORMATION intended only for the use of the
individual or entity named above. If the reader of this message is not the
intended recipient, you are hereby notified that any dissemination,
distribution and copying of this communication is strictly prohibited. If
you have received this communication in error, please immediately notify
the
sender by electronic mail. Thank you.
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of David D. Hillman
Sent: Thursday, January 19, 2006 4:30 PM
To: [log in to unmask]
Subject: Re: [TN] Soldering matte tin over nickel plating
Hi John! A white deposit on a matte tin finish can not be a good thing and
is not normal for the matte tin finishes I am familiar with. I would
subject the components to the JSTD-002B Test S (Surface Mount Simulation
test) to see if it passes. If it fails then you have leverage with your
vendor based on data and not observation. Good Luck.
Dave Hillman
Rockwell Collins
[log in to unmask]
John Burris
<johnhburris@GMAI
L.COM> To
Sent by: TechNet [log in to unmask]
<[log in to unmask]> cc
Subject
01/19/2006 08:54 [TN] Soldering matte tin over
AM nickel plating
Please respond to
TechNet E-Mail
Forum
<[log in to unmask]>
; Please respond
to
John Burris
<johnhburris@GMAI
L.COM>
Dear TechNetters,
We are just starting our journey into lead-free (we are currently covered
under Article 9, but we can see the handwriting on the wall), and we are
starting to deal with some issues as suppliers are making component changes
to comply with RoHS. The component at issue is a heat sink for a TO-220
transistor. Flux is 2% no-clean. Solderability is not good; partial solder
adhesion (about 20-30%) on the mounting tabs. 90% coverage is required by
standards. The matte tin finish appears to have a white deposit that can
be
removed by either scraping or cleaning with a mild solvent. Vendor says
this
is normal and should not affect solderability.
Thoughts?
John Burris
Automated Logic
1150 Roberts Blvd.
Kennesaw, GA 30144-3618
01.770.795.4827 (Office)
01.770.795.3527 (Facimile)
01.404.431.9109 (Cellular)
--
No virus found in this outgoing message.
Checked by AVG Free Edition.
Version: 7.1.375 / Virus Database: 267.14.20/233 - Release Date: 1/18/2006
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|