Re: Gold plated components, what a pain!!
From:
Werner Engelmaier <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Date:
Fri, 11 Nov 2005 08:06:00 EST
Content-Type:
text/plain
Parts/Attachments:
text/plain (28 lines) 
In a message dated 11/11/05 5:37:59, [log in to unmask] writes:

> But Werner,
> the 150 A is over Pd, does the Pd have different properties in terms 
> of oxidization, hence, soldering?
> just for my understanding.
> THX,
> Ivan
> 

While the Pd characteristics are not as established as those of Au and Ag, Pd 
is quite   similar to Au and Ag and one should not be surprised that there is 
Pd-embrittlement besides Au-embrittlement and Ag-embrittlement.



Werner

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2