Subject:
From:
Jerry Dengler <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, Jerry Dengler <[log in to unmask]>
Date:
Wed, 19 Oct 2005 15:25:26 -0400
Content-Type:
text/plain
Parts/Attachments:
text/plain (332 lines)
I don't mean to correct such an accomplished comedian but it's "out
standing in his field" not outstanding.
Jerry 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Whittaker, Dewey
(AZ75)
Sent: Wednesday, October 19, 2005 3:14 PM
To: [log in to unmask]
Subject: Re: [TN] Delamination at Thermal Via area?

So if you did this right you would be a good farmer. Great, I always
wanted to be known as a man outstanding in his field.
Dewey 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Karl Sauter
Sent: Wednesday, October 19, 2005 12:07 PM
To: [log in to unmask]
Subject: Re: [TN] Delamination at Thermal Via area?

Dwight,

In many of our applications the copper plating over the via fill (fill
material is NOT conductive) is needed to create a solderable pad for the
solder joint forming above it that connects to a BGA device, or for good
electrical contact to a socket.  Therefore new assembly techniques may
be needed to prevent excessive underlying laminate material heating
rates as described in thermal via farm areas (good description).

Regards,
Karl Sauter, Sun Microsystems


Dwight Mattix wrote:
> At 08:47 AM 10/19/2005, Karl Sauter wrote:
>
>> Dwight,
>>
>> How is heat to get from the device to the thermal via if you don't 
>> plate over it?
>
>
> The via is plated, yes?
> The via is connected to the surface copper at the knee of the hole,
yes?
> The thermal path is down through the knee of the hole into the via,
yes?
> Any plating over the via fill is a small to insignificant part of the 
> total % surface copper and therefore a small part of the thermal path 
> into the via, no?
>
> Been there, done that, got the T-shirt.  It works.
>
> (warning Will Robinson) When using thermal via farms, you may find any

> solution is so effective at conducting heat into the pwb that without 
> a thoroughly dried pwb, and a carefully controlled preheat/ramp the 
> pwb will be sensitive/prone to delam in those areas anyway.  The risk 
> is accentuated when there's a high % of gnd fill on inner layers in 
> the area.  These via farms w/ gnd fill is really good at passing heat 
> into the pwb fast and creating an unintentional thermal shock effect.
>
> The delam risk is ESPECIALLY high in this type via cluster when uVia 
> buildup layers are needed. Of course the uVia probably means use of 
> single ply dielectrics over buried via subassemblies.  In those cases 
> the plating thickness on the sub needs to be minimized (more is 
> definitely not better), the buried vias need to be prefilled w/ resin 
> to prevent local resin starvation in the single ply layers.
> Otherwise, the single ply will have to stick to tall copper and do it 
> w/out all the necessary resin (avoid 106 in this case and use at least
a 1080).
>
> that's $.04 from me today.  Still free and worth every penny.  :^)
>
> cheers,
> dw
>
>
>
>
>>  Agree that CTE of the non-conductive fill must be a very close
match.
>>
>> Regards,
>> Karl Sauter, Sun Microsystems
>>
>>
>> Dwight Mattix wrote:
>>
>>> We have a lot of experience w/ this type failure.  I'm working on 
>>> the assumption that there's a thermal via farm in that center gnd
slug area.
>>> A couple recommendations ff the cuff...
>>>    * Stay away from conductive via fill material whenever possible
when
>>> vias are tightly packed in "thermal via farms."   Conductive fill is
>>> almost
>>> never needed -- adds very little actual thermal/conductive benefit.
>>> We've
>>> modeled it and test it.  For my money, conductive fill is almost 
>>> always a waste of time and a real pain in the patootie from 
>>> reliability standpoint.
>>> The biggest benefit is that it's easier to plate over and get good 
>>> copper adhesion and that usually only matters on probe sites. Esp 
>>> evil/unpredictable in this application is CB100 (I've had lots of 
>>> dialogue w/ Dupont over the years on this type failure).
>>>    * Use a non-conductive fill that's more closely matched in CTE 
>>> (e.g.San
>>> eh) and don't overplate the fill.
>>>    * Arguably the most significant factor:  don't plate over the 
>>> thermal vias.  All overplating does is give the fill something to 
>>> push against and force the whole plated area up during thermal 
>>> excursions. It's like screwing a cylinder head on tightly and then 
>>> pushing all the pistons up against it (expanding fill at temp).  Pop

>>> goes the weasel!  Overplating doesn't add any grounding or thermal 
>>> benefit. The solder joint in the gnd slug will still be fine w/ the 
>>> dot pattern that emerges.
>>>    * As a work around/mod: We've eliminated a couple of these 
>>> problems on finished product by just etching or laser ablating a dot

>>> of copper off over the fill.
>>> there's my $.02.  Free and worth every penny.  ;^) cheers, dw At 
>>> 07:29 AM 10/19/2005, Steve Gregory wrote:
>>>
>>>> Hi Wee Mei!
>>>>
>>>> I've got your pictures posted. Go to:
>>>>
>>>> http://www.stevezeva.homestead.com/files/U2_top.JPG
>>>> http://www.stevezeva.homestead.com/files/U2_bottom.JPG
>>>> http://www.stevezeva.homestead.com/files/U2_delamination.JPG
>>>>
>>>> Are the vias filled? Are you seeing this delamination on very many 
>>>> PCB's? Are you seeing it only on the bottom of the PCB?
>>>>
>>>> Kind regards,
>>>>
>>>> -Steve Gregory-
>>>> Senior Process Engineer
>>>> LaBarge Incorporated
>>>> Tulsa, Oklahoma
>>>> (918) 459-2285
>>>> (918) 459-2350 FAX
>>>>
>>>>
>>>>
>>>> |---------+---------------------------->
>>>> |         |           Wee Mei          |
>>>> |         |           <[log in to unmask]
>>>> |         |           SG>              |
>>>> |         |           Sent by: TechNet |
>>>> |         |           <[log in to unmask]>|
>>>> |         |                            |
>>>> |         |                            |
>>>> |         |           10/19/2005 03:47 |
>>>> |         |           AM               |
>>>> |         |           Please respond to|
>>>> |         |           TechNet E-Mail   |
>>>> |         |           Forum            |
>>>> |         |           <[log in to unmask]>|
>>>> |         |           ; Please respond |
>>>> |         |           to Wee Mei       |
>>>> |         |           <[log in to unmask]
>>>> |         |           SG>              |
>>>> |         |                            |
>>>> |---------+---------------------------->
>>>>
>>>>
>>>>  
>>>> >------------------------------------------------------------------
>>>> --------------------------------------------|
>>>>
>>>>
>>>>   |
>>>>                                         |
>>>>   |       To:       [log in to unmask]@SMTP@Exchange
>>>>                                         |
>>>>   |       cc:       (bcc: Stephen R
>>>> Gregory/LABARGE)
>>>>
>>>> |
>>>>   |       Subject:  [TN] Delamination at Thermal Via
>>>> area?                                                       |
>>>>
>>>>
>>>>  
>>>> >------------------------------------------------------------------
>>>> --------------------------------------------|
>>>>
>>>>
>>>>
>>>>
>>>>
>>>> Hello,
>>>>
>>>> Just asked Steve to download 3 pictures on the defects. Kindly take

>>>> a look at them and would appreciate some feedback on the possible 
>>>> root cause.
>>>>
>>>> Steve : Thanks for the downloading.
>>>>
>>>> Regards,
>>>> Wee Mei
>>>>
>>>> ---------------------------------------------------
>>>> Technet Mail List provided as a service by IPC using LISTSERV 1.8e 
>>>> To unsubscribe, send a message to [log in to unmask] with following 
>>>> text in the BODY (NOT the subject field): SIGNOFF Technet To 
>>>> temporarily halt or (re-start) delivery of Technet send e-mail to
>>>> [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE 
>>>> mailing per day of all the posts: send e-mail to
>>>> [log in to unmask]: SET Technet Digest Search the archives of 
>>>> previous posts at:
>>>> http://listserv.ipc.org/archives
>>>> Please visit IPC web site
>>>> http://www.ipc.org/contentpage.asp?Pageid=4.3.16
>>>> for additional information, or contact Keach Sasamori at 
>>>> [log in to unmask] or 847-615-7100 ext.2815
>>>> -----------------------------------------------------
>>>>
>>>>
>>>>
>>>> __________________________________________________________________
>>>> This message may contain information that is privileged and 
>>>> confidential to LaBarge, Inc.  It is for use only by the individual

>>>> or entity named above.
>>>> If you are not the intended recipient, you may not copy, use or 
>>>> deliver this message to anyone.  In such event, you should destroy 
>>>> the message and kindly notify the sender by reply e-mail.
>>>>
>>>> ---------------------------------------------------
>>>> Technet Mail List provided as a service by IPC using LISTSERV 1.8e 
>>>> To unsubscribe, send a message to [log in to unmask] with following 
>>>> text in the BODY (NOT the subject field): SIGNOFF Technet To 
>>>> temporarily halt or (re-start) delivery of Technet send e-mail to
>>>> [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE 
>>>> mailing per day of all the posts: send e-mail to
>>>> [log in to unmask]: SET Technet Digest Search the archives of 
>>>> previous posts at:
>>>> http://listserv.ipc.org/archives
>>>> Please visit IPC web site
>>>> http://www.ipc.org/contentpage.asp?Pageid=4.3.16
>>>> for additional information, or contact Keach Sasamori at 
>>>> [log in to unmask] or 847-615-7100 ext.2815
>>>> -----------------------------------------------------
>>>
>>>
>>> ---------------------------------------------------
>>> Technet Mail List provided as a service by IPC using LISTSERV 1.8e
>>> To unsubscribe, send a message to [log in to unmask] with following
>>> text in
>>> the BODY (NOT the subject field): SIGNOFF Technet
>>> To temporarily halt or (re-start) delivery of Technet send e-mail to
>>> [log in to unmask]: SET Technet NOMAIL or (MAIL)
>>> To receive ONE mailing per day of all the posts: send e-mail to
>>> [log in to unmask]: SET Technet Digest
>>> Search the archives of previous posts at:
>>> http://listserv.ipc.org/archives
>>> Please visit IPC web site
>>> http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
>>> information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100
>>> ext.2815
>>> -----------------------------------------------------
>
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following text
in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
http://listserv.ipc.org/archives
> Please visit IPC web site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
> information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100
> ext.2815
> -----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2