Sender:
X-To:
Date:
Wed, 12 Oct 2005 13:21:18 -0400
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Subject:
From:
Werner Engelmaier <[log in to unmask]>
In-Reply-To:
<200510111305937.SM02952@cpujoel0224>
MIME-Version:
1.0
Content-Type:
text/plain; charset="us-ascii"; format=flowed
Parts/Attachments:
text/plain (124 lines)
Hi Joel,
I do agree with Lee Parker. I am glad you had no problems with
ENIG--many of my cients were not this lucky.
Werner Engelmaier


-----Original Message-----
From: Joel Mearig <[log in to unmask]>
To: [log in to unmask]
Sent:         Tue, 11 Oct 2005 12:54:21 -0700
Subject: Re: [TN] Hasl

   Lee,
Good input that I agree with. However, I was wondering if you could
further
discuss the "flash" vs. "ENIG" issue. I have been using ENIG on my
Pb-free
assemblies for about 7 years with very little problems. If I am missing
something further education would be extremely helpful. Thanks

Joel Mearig
Delta Tau Data Systems, Inc.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Lee parker
Sent: Tuesday, October 11, 2005 10:03 AM
To: [log in to unmask]
Subject: Re: [TN] Hasl

Ramon

After reflowing a soldered surface, you will form a meniscus which will
interfere with SMT component placement. To avoid the problem I suggest a
flat metal finish such as immersion silver or flash gold (not ENIG)

Best regards
Lee

J. Lee Parker, Ph.D.
JLP Consultants LLC
804 779 3389
  ----- Original Message -----
  From: Dehoyos, Ramon<mailto:[log in to unmask]>
  To: [log in to unmask]<mailto:[log in to unmask]>
  Sent: Tuesday, October 11, 2005 12:52 PM
  Subject: [TN] Hasl



              Hi technetters:
              Is there a fine pitch limit  to the use of HASL board
plating
  finish due to its variation in thickness?  Does selective solder strip
  and reflow plating, SSSR, have a significant advantage over HASL? Any
  comments relating to platting finish would be greatly appreciated. I
  thank you for your comments.
          Ramon
          ME
          410.552.2210

  ---------------------------------------------------
  Technet Mail List provided as a service by IPC using LISTSERV 1.8e
  To unsubscribe, send a message to
[log in to unmask]<mailto:[log in to unmask]> with following text in
  the BODY (NOT the subject field): SIGNOFF Technet
  To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]<mailto:[log in to unmask]>: SET Technet NOMAIL or (MAIL)
  To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]<mailto:[log in to unmask]>: SET Technet Digest
  Search the archives of previous posts at:
http://listserv.ipc.org/archives<http://listserv.ipc.org/archives>
  Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16<http://www.ipc.org/conte
ntp
age.asp?Pageid=4.3.16> for additional information, or contact Keach
Sasamori
at [log in to unmask]<mailto:[log in to unmask]> or 847-615-7100 ext.2815
  -----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2