I haven't woke-up yet, strike that last question.
You said you already recieved the boards...
so you would know if you got new ones or not.
Kind regards,
-Steve Gregory-
Senior Process Engineer
LaBarge Incorporated
Tulsa, Oklahoma
(918) 459-2285
(918) 459-2350 FAX
Stephen R Gregory/LABARGE@LABARGE
Sent by: TechNet <[log in to unmask]>
09/16/2005 06:16 AM
Please respond to TechNet E-Mail Forum <[log in to unmask]>; Please respond to Stephen R Gregory
To: [log in to unmask]@SMTP@Exchange
cc: (bcc: Stephen R Gregory/LABARGE)
Subject: Re: [TN] Rework for Delaminated PWBs
Mornin' Everybody!
I have the pictures that Mumtaz sent me posted now. Go to:
http://www.stevezeva.homestead.com and click on "Picture Page 2"
and look at; "Blister 1, Blister 2, After Bake 1, and After Bake 2".
Boy, that's some SERIOUS delamination! I don't know enough to say
if the rework that your supplier is proposing is acceptable, but my first
question would be is why would they send you boards that are not cured?
If they sent you boards that are that undercured, what else is wrong with
these boards?
I would have a very hard time accepting these boards. Which brings up
another question, if you say you won't accept them and that you want new
boards, how will you know that you won't get the same boards that your
supplier has "reworked"?
Kind regards,
-Steve Gregory-
Senior Process Engineer
LaBarge Incorporated
Tulsa, Oklahoma
(918) 459-2285
(918) 459-2350 FAX
Mumtaz Bora <[log in to unmask]>
Sent by: TechNet <[log in to unmask]>
09/15/2005 08:20 PM
Please respond to TechNet E-Mail Forum <[log in to unmask]>; Please respond to Mumtaz Bora <[log in to unmask]>
To: [log in to unmask]@SMTP@Exchange
cc: (bcc: Stephen R Gregory/LABARGE)
Subject: [TN] Rework for Delaminated PWBs
Dear Technetters,
We have received a large batch of PWBs that is showing delamination after
reflow at peak temp. 230C. Laminate is high Tg - 170C.
Supplier is proposing to perform the following rework -- on these boards
instead of providing replacement parts.
Oven bake at 190C for 2.5 hours followed by second bake at 150C for 2
hours at 6kg/cm2 pressure. Will this guarantee a full cure?
I am concerned about latent failures and layers opening up as full cure was
not achieved the first time.
Any inputs from the forum will be appreciated.
I will request Steven Gregory to place the image of delamination on his
website. Have a great weekend.
Thank-you
Mumtaz
D/ 252 - SMT Process and Component Quality
Bldg. V238E
Voice (858)-882-1967
Fax (858)-882-3126
Page (858)-635-1180
Cell: (858) -449-7054
email: [log in to unmask]
Kyocera-Wireless Corp.
10300, Campus Point Drive
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
San Diego, Ca 92121,USA
__________________________________________________________________
This message may contain information that is privileged and confidential to LaBarge, Inc. It is for use only by the individual or entity named above. If you are not the intended recipient, you may not copy, use or deliver this message to anyone. In such event, you should destroy the message and kindly notify the sender by reply e-mail.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
__________________________________________________________________
This message may contain information that is privileged and confidential to LaBarge, Inc. It is for use only by the individual or entity named above. If you are not the intended recipient, you may not copy, use or deliver this message to anyone. In such event, you should destroy the message and kindly notify the sender by reply e-mail.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|