Subject:
From:
Lawrence Russell <[log in to unmask]>
Reply To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Date:
Tue, 13 Sep 2005 08:26:19 +0800
Content-Type:
text/plain
Parts/Attachments:
text/plain (56 lines)
Dennis and others,

Your comments are much appreciated on this, the copper was etched before laser drilling, and permanganate desmear. This is Paladium metalization and Revese Pulse plated, so the hole geometry  is what needs addressing, it seems.
Time to back down on the laser power \.../

Larry Russell
-----Original Message-----
From: Dennis Fritz [mailto:[log in to unmask]]
Sent: Monday, September 12, 2005 10:16 PM
To: [log in to unmask]
Subject: Re: [TN] Microvia Puzzle


The microvia you have sectioned will be an enormous problem to  electroplate
- as you have found out.

It appears that very significant etchback of the resin/glass  under the
copper foil has occured. The "shelf" left by the copper surface foil  is requiring
the copper to plate back under itself.  This type of "desmear"  was common
when plasma was used to remove resin only dielectric some years  ago.  The way
the overhang problem was solved was to agressively  microetch the surface foil
to remove all the overhang.  I suggest the same  thing here.

How was the original copper foil removed for this  microvia?  You say CO2,
but it appears to me that too much copper is  present for the CO2 to cut through
it.  Either, this was a combined UV/CO2  microvia drill where the UV cut the
initial foil and the CO2 removed the epoxy  and glass fibers, or the original
hole in the foil was chemically etched.   Notice how the microvia drill
stopped nicely at the level two copper foil - the  way CO2 drills do.

I think your microvia will be easier to plate with more of a  "V" shape, and
certainly no copper foil overhang.

Denny Fritz
MacDermid, Inc.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2