ON NO ACCOUNT would I recommend any abrasive process for this. The only
effect it would have would be to implant adhesive particles into the copper.
Brian
Jeffrey Bush wrote:
> This is not a normal process. I would think that chemical etching is
> more affective in removing metals and oxides from the resin surface. We
> see no issues with SIR/MIR using standard PCB processes. I have done
> this in the past of flex to promote stiffener bonding and mask adhesion.
> Possible the PCB house has an issue with chemical etching or base
> materials.
>
> Jeffrey Bush
> Director, Quality Assurance and Technical Support
>
> VERMONT CIRCUITS INCORPORATED
> 76 Technology Drive - POB 1890
> Brattleboro, Vermont 05302
> Voice: 802.257.4571.21 Fax: 802.257.0011
> http://www.vtcircuits.com
>
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Ivanoe Pedruzzi
> Sent: Tuesday, September 06, 2005 9:35 AM
> To: [log in to unmask]
> Subject: [TN] Sand blasting pcb after copper etching
>
> Dear Technetters,
>
> I'm not familiar with the process of making pcb and I would like to
> have your comments on something I was told from a pcb maker
> representative.
>
> "...in order to ensure a well insulation between traces, we do
> sandblasting (very little and tiny) pcb's after etching.
> this is to remove the bonding material that remains on the board after
> removing the copper. This is the only way to achieve a very good SIR
> result."
>
> Is this a normal procedure, was he correct in his claim?
>
>
> Thanks,
> Ivanoe Pedruzzi
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following text
> in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
> http://listserv.ipc.org/archives
> Please visit IPC web site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
> ext.2815
> -----------------------------------------------------
>
> ---------------------------------------------------
> Technet Mail List provided as a service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
> -----------------------------------------------------
>
--
______________________________________________
Please note new e-mail address [log in to unmask]
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|