Subject:
From:
Richard Kraszewski <[log in to unmask]>
Reply To:
(Leadfree Electronics Assembly Forum)
Date:
Mon, 1 Aug 2005 15:04:06 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (148 lines)
It's the IPC SPVC SAC alloy report.  It runs ~$99 US for IPC members.
Well worth the bucks. Here's the link to the executive summary:

http://www.ipc.org/3.0_Industry/3.5_Councils_Associations/3.5.1_Industry
_Assoc/spvc_bro/SVPC_Final_ExecSumm.pdf

Rich - KEDS

 
 

-----Original Message-----
From: Leadfree [mailto:[log in to unmask]] On Behalf Of No Name
Sent: Monday, August 01, 2005 1:55 PM
To: [log in to unmask]
Subject: Re: [LF] 96.5% Tin / 3.5% Silver vs. SAC305

Based on testing we have done the 96.5 Sn/3.5 Ag will behave very close
to
the SAC alloys in wavesolder and it doesn't take long to pick up some
copper and then its just like SAC 305. I have heard some say that you
may
get more voiding is SMT than you do with the SAC alloys.
Can you tell me where to get a copy of this test report?





Ken Kirby
Applications Engineer
Speedline Technologies
573-346-3341 ext 162
cell 817-946-3357



             Richard
             Kraszewski
             <[log in to unmask]
To
             COM>                      [log in to unmask]
             Sent by: Leadfree
cc
             <[log in to unmask]
             >
Subject
                                       [LF] 96.5% Tin / 3.5% Silver vs.
                                       SAC305
             08/01/05 11:17 AM


             Please respond to
                "(Leadfree
                Electronics
             Assembly Forum)"
             <[log in to unmask]
             >; Please respond
                    to
                  Richard
                Kraszewski
             <[log in to unmask]
                   COM>






Just reviewed the IPC SPVC report on the SAC alloys.  2 thumbs up on
that effort!!!  Now for the question at hand.



Seeing that there seemed to be little performance difference amongst the
3 alloys being considered, what if you go one step further.  Would all
of you think that an alloy such as 96.5 Sn/3.5 Ag would perform equally
well?  Sure the melt point is ~ 4 degC higher , but with some copper
contamination whether it be in a TH or SM, won't you think the
performance would be very similar to say SAC305?



Reason I'm asking is that I'm supporting some 96.5% Tin / 3.5% Silver
processes, and need to determine if I switch them over to SAC305 or let
them continue as they are.



Your thoughts would be appreciated.



Rich K KEDS












------------------------------------------------------------------------
-------Leadfee
 Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks
send:
SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or
847-615-7100 ext.2815
------------------------------------------------------------------------
-------

------------------------------------------------------------------------
-------Leadfee Mail List provided as a service by IPC using LISTSERV
1.8d
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks
send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
------------------------------------------------------------------------
-------

-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------

ATOM RSS1 RSS2