Hi all,
Just like to know whether anyone has done Lead Free Selective Soldering.
Did you have any issues or difficulties?

Secondly on LF dross. I read somewhere that the density of LF dross is
greater than SnPb and the LF alloy, it will sink instead of float. However a
source who are using LF solders have told me otherwise.

Is this a big issue, if an issue? How would you handle this?

Regards
Dennis Bang


#################################################
***** CONFIDENTIAL *****
We apologise if this message has been sent to you in error.  We are
committed to protecting the confidential information of our customers,
our vendors and GPC Electronics.  If you have received this message in
error, we would appreciate you removing it from your system and
informing us of the error, so that we may continue to improve our
processes.
Please note that whilst we check our outgoing mail, you should also
check any attachments for viruses and defects before opening them or
sending them on.
Thank you.
#################################################

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------