It's a matter of cost. SAC alloys can be well used in wave soldering at
almost the same wave temperature as SnPb but ist more expensive than
SnPb. SnCu(Ni) is cheaper than SAC with the drawback of higher
temperature plus having another alloy in the wave joints than in the
reflow joints.
Best regards
Guenter
EMPA
Swiss Federal Laboratories for Materials Testing and Research
Centre for Reliability
Guenter Grossmann, Senior Engineer
8600 Duebendorf
Switzerland
Phone: xx41 1 823 4279
Fax : xx41 1 823 4054
mail: [log in to unmask]
>>> [log in to unmask] 10.05.2005 19:19:59 >>>
Technet,
Can anyone share what the differences are between
Tin-Silver-Copper (SAC) solder and the Tin-Copper-Nickle solder
(or ultimately, the solder joints) for use in wave solder machines?
Why would someone want to use one over the other?
Thanks,
Kaye
CONFIDENTIALITY NOTE: This message is intended only for the use of the
individual or entity to which it is addressed and may contain
information that is privileged, confidential, and exempt from disclosure
under applicable law. If the reader of this notice is not the intended
recipient, you are hereby notified that any dissemination, distribution
or copying of this communication is strictly prohibited. If you have
received this communication in error, please notify the sender
immediately.
_____________________________________________________________________________
Scanned by IBM Email Security Management Services powered by
MessageLabs. For more information please visit http://www.ers.ibm.com
_____________________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|