There is no issue with lead being present in a process just so long as there is no lead in the final RoHS compliant product being sold.
RoHS is intended to prevent lead (in waste electronic product - WEEE) going into landfill, as it has been identified that WEEE makes up a significant proportion of landfill.
Lead will still be used in accumulators etc. - in fact that's where most lead is used. The difference is that accumulators (car batteries) are recycled so the lead does not end up in landfill.
Regards,
Chris
____________
-----Original Message-----
From: Leadfree [mailto:[log in to unmask]] On Behalf Of Smith, Rick
Sent: 25 May 2005 14:16
To: [log in to unmask]
Subject: Re: [LF] Pb Sn Stripped PCB and Rohs
We are, ENIG is a cost adder.
But that will be our next project after getting the remaining RoHS/WEEE Directives implemented.
-----Original Message-----
From: Leadfree [mailto:[log in to unmask]] On Behalf Of Edward Szpruch
Sent: Wednesday, May 25, 2005 2:00 AM
To: [log in to unmask]
Subject: Re: [LF] Pb Sn Stripped PCB and Rohs
Tin-lead is used as etch resist for alkaline etching of pattern plated
PCB.After etching is stripped out.Completly.
No left-overs.What does this process has in common with RoHS ??? There is NO
lead on the PCB.
The same is applied, for example, to Cyanide. ENIG finishing is involved in
dipping the board in Cyanide containig Gold solution.Very toxic and very
powerfull poison.
Anyone is considering ban on ENIG finishing ???
Edward
> -----Original Message-----
> From: MA/NY DDave [SMTP:[log in to unmask]]
> Sent: ד מאי 25 2005 7:19
> To: [log in to unmask]
> Subject: Re: [LF] Pb Sn Stripped PCB and Rohs
>
> Hi Roger, Mike, IPC LF Listservers,
>
> Thanks,
>
> I don't know all of the other EU Directives, particularly for those living
> and working in the EU production industries. My expectation is that since
> the EU is coming after lead in electrical and electronic equipment they
> have already or will go after lead in the process and manufacturing
> industries when a replacement process exists.
>
> Considering the date associated with the Whereas. That is some meeting or
> resolution on 30Jul96 or 1996.07.30 my thought was that there should
> already be on the books other directives limiting lead. I don't know yet
> hope MikeF, and I believe Roger who live in the EU, are correct that this
> isn't legislated yet in the EU.
>
> Why isn't this process of tin lead as an etch resist, and then later
> completely stripped rather than reflowed for superbe long term storage and
> solderability, on a replacement list?
>
>
> Yours in Engineering, Dave
> YiEngr, MA/NY DDave
>
> --------------------------------------------------------------------------
> -----Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Leadfree
> To temporarily stop/(start) delivery of Leadree for vacation breaks send:
> SET Leadfree NOMAIL/(MAIL)
> Search previous postings at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at [log in to unmask] or
> 847-615-7100 ext.2815
> --------------------------------------------------------------------------
> -----
-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------
-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------
-----------------------------------------
This message (including any attachments) may contain confidential
information intended for a specific individual and purpose. If you are not
the intended recipient, delete this message. If you are not the intended
recipient, disclosing, copying, distributing, or taking any action based on
this message is strictly prohibited.
-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------
|