I now have a couple of cross sections to go along with my
xrays.
Does anyone have an idea what might cause this type of anomaly?
http://www.texas-gold.org/PCB/pages/xray/index.htm
Is this a problem or just a strange looking void ?
The board supplier is going to run the following tests
* Cross section the 15 pin connector area for optical
microscopy and analysis.
* Scanning Electron Microscopy (SEM) analysis of solder
filled and bare silver hole wall surfaces
o SEM will identify particulate or other 3-dimensional
bodies to be analyzed with EDS.
* Energy Dispersive Spectometry (EDS) analysis of
solder filled and bare silver hole wall surfaces
o EDS will identify the all elements relative to the
point of failure to identify possible contributors as the root cause.
* X-Ray Fluorescence of bare silver hole wall surfaces
o XRF will determine the thickness of the solder deposit
in the hole walls in the 15 pin connector area.
-Al
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------