John, need immediate advice from you, as you are being very familiar with ceramic caps.
Got problem with 0603 100nF/16VDC/X7R, Rins > 10-100 kOhms, sometimes lower. Failure rate 1-2%.
Q: Terminals AgCuNiSnPb instead of usual AgNiSnPb. Never seen Cu before. Why Cu?
Thx in advance
Ingemar Hernefjord
Ericsson Microwave Systems
---------------------------------------------------