We have some LCCC's that needed gold removal, and we did them here
in house manually. The lady that I had doing this was really careful, but
she
got some solder on top of a few of them.

QA was wanting to scrap them because of "solder contamination". I disagree
that they should be scrapped. I can't find any spec that says they need to
be
scrapped. You can still read the part numbers, and there are no solder
shorts
from the castellations to the top. Go to:

http://www.stevezeva.homestead.com

and look at "Solder on LCCC", and tell me what you think....these are
$50.00 ea.
and I don't want to scrap them if I don't have to.

Kind regards,

-Steve Gregory-
Senior Process Engineer
LaBarge Incorporated
Tulsa, Oklahoma
(918) 459-2285
(918) 459-2350 FAX
__________________________________________________________________
This message may contain information that is privileged and confidential to
LaBarge, Inc.  It is for use only by the individual or entity named above.
If you are not the intended recipient, you may not copy, use or deliver
this message to anyone.  In such event, you should destroy the message and
kindly notify the sender by reply e-mail.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------