F&K 6400 made this special job.
Our K&S or Palomar not quite so good.
http://www.sitest.co.uk/F&K_wirebonders.htm
/Ingemar
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]
Sent: den 14 januari 2005 17:03
To: [log in to unmask]
Subject: Re: [TN] FAB - Al Wire Bonding
Ingemar,
I thought they were very nice shots as well!!
What bonder/s? :-)
Steve
-----Original Message-----
From: Ingemar Hernefjord (KC/EMW)
[mailto:[log in to unmask]]
Sent: Friday, January 14, 2005 10:47 AM
To: [log in to unmask]
Subject: Re: [TN] FAB - Al Wire Bonding
No, dear laser woman, doesn't drop performance <1GHz. Short loop=testing worst conditions.
No gold=less cost. Cute pic? What associations do you get? Haggish or Bratwurst?
Inge
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Joyce Koo
Sent: den 14 januari 2005 15:22
To: [log in to unmask]
Subject: Re: [TN] FAB - Al Wire Bonding
IngeMAR,
why Ni? Isn't it effect your performance? I guess it is not signal, it
should be OK.
Very cute photo... the thicker wire almost shaped to square, is it
intentional deformation by the capillary? Thx.
jk
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Steve Gregory
Sent: Thursday, January 13, 2005 10:57 PM
To: [log in to unmask]
Subject: Re: [TN] FAB - Al Wire Bonding
Hi All!
I just got Inge's pictures up...sorry for being so tardy. I'm going through
J-STD-001 and IPC-7711/7712 Instructor certification out here in
California,
and only get to my 'pooter when I get back to my hotel room after school.
Go to: _http://www.stevezeva.homestead.com_
(http://www.stevezeva.homestead.com) and look at Bond 1 - 5
-Steve Gregory-
Al fine wire, signal only, isn't very demanding, but heavy Al wire (50um
and
up) combined with high currents can be schrecklich, as Werner would say.
Too
thick gold and impurities can cause bond lifting after some time of
operating at high temperature. If you are uncertain, I'd recommend a night
or two in
bed reading Harman's wire bonding Bible.
I anticipate that you aim at wedge bonding. In fact we've found that you
can
bond successfully on nickel without any gold at all (don't take it as a
recommendation, but just as information). We let the autobonder make
thousands of
fine wire Al bonds on nickelplated aluminium plates, not one single
missing,
and wire pull test statistics looked just fine.
Asked Steve to hang some typical pics on the wall FYI. Not best quality
images, but give you an idea. Two pics 37um and the others 125 um Si-doped
Al
wire. Interesting to see what other's think about bonding directly on
nickel
like this....
Ingemar Hernefjord
Ericsson Microwave Systems
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of John Parsons
Sent: den 13 januari 2005 00:32
To: [log in to unmask]
Subject: [TN] FAB - Al Wire Bonding
Greetings all,
I am trying to learn something about the wire bonding process. Our
customer
has a part on which they spec the finish of some edge connector fingers as
"Gold Plated for Wire Bonding Al Wire". As we do not provide a wire
bondable gold finish in-house we have subcontracted the service. The
plating service tells me that typically for Al wire bonding all that is
required is a typical ENIG process (5-10u" Au over 200u" Ni). I believe
that in past verbal communications with the customer they have said that an
ENIG finish would not suffice and that they require 15u" of bondable gold
(electroless gold or electroplated??) .
What say you? Or does "it depend" :-)
Regards
John Parsons
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|