Carrie,

Some info from one SM mfr, this may help.

http://www.enthone.com/electronics/pdf/Imup5.pdf

-- Gregg

At 02:27 PM 4/22/2004, Morse, Carrie wrote:
>Here's the status.  I baked the boards for 45min @ 250F and...I still
>have the white haze.  No change.  So, What do you all think?
>(IOW--HELP!!!!)
>
>-Carrie
>
>-----Original Message-----
>From: Brian Ellis [mailto:[log in to unmask]]
>Sent: Thursday, April 22, 2004 2:06 AM
>To: TechNet E-Mail Forum.; Morse, Carrie
>Subject: Re: [TN] White Discoloration -- Excessive Heat, Insufficiently
>Cured SM, or, Both?
>
>I'm not saying that this is the cause, but another possibility is
>hydrolysis of the uncured solder mask. If the boards are coated and then
>stored in a humid atmosphere before development (either before or after
>exposure) for more than an hour or two, then some components in the
>chemistry may absorb sufficient humidity to hydrolyse, partially
>upsetting the polymerisation.
>
>I suggest methylene chloride would be better than acetone for a wipe
>test, but it depends on the chemistry of the LPI.
>
>Brian
>
>Morse, Carrie wrote:
> > We are wave soldering a LPI board and seeing a Whitish Discoloration
> > -- Haze like -- only in the areas that the board has seen OA flux and
>wave.
> > We are using a wave pallet and the areas not exposed do not exhibit
> > this phenomena.  This board is also processed through SMT for one side
>
> > and we do not see this around any of the SMT.
> >
> > We have not seen this problem in the past, and, the Wave operator
> > states that the wave recipe has not changed.
> >
> > So, I am wondering -- if LPI is not fully cured, will it turn white
> > when exposed to OA flux and Wave?
> > Also, what IS the max temp LPI should be able to see and for how long
> > without discoloring?
> > We've done an Acetone test, but, it comes up clean and....I think I
> > read in a previous posting that the Acetone may not be an effective
> > test for LPI.  Is that true?  If so, What IS an effective test?
> >
> > I'm headed to the Omega tester to see "how clean" the board is.
> >
> > All advice is welcome!
> >
> > -Carrie
> >

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------