Subject:
From:
Jack Crawford <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Fri, 12 Sep 2003 09:37:16 -0500
Content-Type:
text/plain
Parts/Attachments:
text/plain (128 lines)
More information about IPC's Annual Meeting and the technical conference
mentioned below at http://www.ipc.org/contentpage.asp?Pageid=5.4

Thanks
Jack
 

-----Original Message-----
From: Dave Hillman [mailto:[log in to unmask]] 
Sent: Thursday, September 11, 2003 11:36 AM
To: [log in to unmask]
Subject: Re: [TN] Zinc Plating Finish


Hi TechNet! Steve - you have fallen into the galvanic series trap! There
is
the potential for a galvanic reaction between Zn and Sn but there are
several other factors which need to be considered - the Galvanic Series
chart is only a first order approximation of a possible reaction. Your
cathode-to-anode ration, the type/use of coatings (postcoat, chem film),
the "chemistry" of the use environment, and how "sealed" the electronic
assembly is designed all play a role in the amount and type of corrosive
attack on the Zn plating. There will be a paper at the IPC Fall meeting
on
the subject of galvanic compatibility of the new immersion finishes and
aluminum which may be helpful.

Dave Hillman
Rockwell Collins
[log in to unmask]




                      Steve Gregory
                      <[log in to unmask]        To:       [log in to unmask]
                      m>                       cc:
                      Sent by: TechNet         Subject:  Re: [TN] Zinc
Plating Finish
                      <[log in to unmask]>


                      09/11/2003 11:16
                      AM
                      Please respond to
                      "TechNet E-Mail
                      Forum."; Please
                      respond to
                      SteveZeva






Hi Victor!

What will probably happen is that the Zinc will start to corrode because
of
the galvanic action between itself and the tin, or tin / lead. Go to:

http://www.ccfast.com/ccfcorrosion.html

There you will see a Galvanic Series chart, and a simple explaination
about
Galvanic action. Zinc, and Tin or Tin / Lead isn't all that far apart in
the chart, but far enough that the Zinc will corrode.

-Steve Gregory-


 Fellow TechNetters:

    What are the exposures of having or selecting a ZINC plating finish
for
 an ELECTRICAL CONTACT such as a solder less
 crimp connector and straight pin connector.   What can occur if these
 finishes are mixed mated with a SnPb or Sn finish surface.

 Victor,



---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask]
or
847-509-9700 ext.5315
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------

ATOM RSS1 RSS2