TECHNET Archives

May 2003

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
Bev Christian <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Fri, 30 May 2003 17:07:22 -0400
Content-Type:
text/plain
Parts/Attachments:
text/plain (67 lines)
Rich,
Yes I am aware of that part. I should have said so in my e-mail. Someone is suggesting for the condition stated that it is relaxed even further! I am not aware of any such provision. 
Bev
--------------------------
Sent from my BlackBerry Wireless Handheld (www.BlackBerry.net)


-----Original Message-----
From: Rich Lasko <[log in to unmask]>
To: 'TechNet E-Mail Forum.' <[log in to unmask]>; Bev Christian <[log in to unmask]>
Sent: Fri May 30 17:08:27 2003
Subject: RE: [TN] PTH Hole Fill

Bev,

I don't recall seeing any statements verbatim to what you've described below
but see section 6.3.1 (Fig. 6-6) of A610 Rev. C and section 9.2.5.1 of
J-STD-001C.  These sections do talk about allowable solder depression  (up
to a maximum of 25%).  But I would also recommend finding out what type of
environment the assembly will end up in.  High vibratory and/or thermal
shock environments may need further review before stating that such solder
depression is okay.  Hope this helps.

Rich Lasko
Badger Electronics

-----Original Message-----
From: Bev Christian [mailto:[log in to unmask]] 
Sent: Friday, May 30, 2003 3:49 PM
To: [log in to unmask]
Subject: [TN] PTH Hole Fill

Technetters,
Someone in our company is quite sure "there was a relaxation of solder fill
when and if the lead of the component was not sufficiently large enough
compared to the PTH to which it was soldered".  I have no recollection of
such a change in A610. But the maybe some of my brain cells are on vacation.
Can anyone comment on the statement about hole fill, please?  Thanks.

Bev Christian
Research in Motion

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------

ATOM RSS1 RSS2