TECHNET Archives

April 2003

TechNet@IPC.ORG
Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
TechNet <[log in to unmask]>
X-To:
[log in to unmask]
Date:
Thu, 10 Apr 2003 17:07:46 -0400
Reply-To:
"TechNet E-Mail Forum." <[log in to unmask]>, [log in to unmask]
Subject:
Too Much No Clean
MIME-Version:
1.0
Content-Transfer-Encoding:
8bit
Content-Type:
text/plain; charset=iso-8859-1
From:
Neda Thrash <[log in to unmask]>
Parts/Attachments:
text/plain (15 lines) 
Hello Technetters!
I often observe rework/touchup operators drenching the area of a PCB they are soldering with no clean flux. When the flux spreads to an area not heated by the soldering iron or washed away, what long term effect will this have? Will it affect only certain designs or would this be a problem for most?
TIA for your help!

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------

ATOM RSS1 RSS2