Good Morning Bev,
I think I have seen the exact condition you describe. Question; Is the
component a chemical etched Rf shield?
If so what you are seeing is probably residue from the fabrication process.
As far as I know the condition is cosmetic, i.e. doesn't affect
solderability. I consider it a process indicator and contact the vendor when
we see it.
Good Luck,
Dan
---------------------------------------------------