Subject:
From:
Mike Fenner <[log in to unmask]>
Reply To:
Date:
Thu, 27 Feb 2003 16:46:27 -0000
Content-Type:
text/plain
Parts/Attachments:
text/plain (95 lines)
Keeping the time over liquidus as short as possible and rapid cooling as
possible will help, subject to the possibilities of your system

Regards

Mike Fenner

Applications Engineer, European Operations
Indium Corporation
 T: + 44 1908 580 400
M: + 44 7810 526 317
 F: + 44 1908 580 411
 E: [log in to unmask]
W: www.indium.com
Leadfree: www.Pb-Free.com



-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Morse, Carrie
Sent: Thursday, February 27, 2003 3:57 PM
To: [log in to unmask]
Subject: Re: [TN] : Shining smooth solder joint on ENIG or Gold plating
Board.


Poh,
Although shiny joints are not an IPC/J-STD requirement, you can minimize
dullness by using nitrogen in your oven, or, by changing solder pastes.
Some pastes provide for shinier joints than others.  But again, shininess is
not a requirement.

-Carrie

-----Original Message-----
From: Poh Kong Hui [mailto:[log in to unmask]]
Sent: Thursday, February 27, 2003 7:18 AM
To: [log in to unmask]
Subject: [TN] : Shining smooth solder joint on ENIG or Gold plating
Board.
Importance: High


Hi Technetters,

Can someone advise me how to get a good smooth shining solder joint on the
ENIG board or board with gold plate SMT pads.

As I can understand that board subjected to reflow soldering, the solder
joint tends to look dull and not so smooth joint. But, is there any way to
get a good shining joint.

Thanks.

Poh

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------

ATOM RSS1 RSS2