Could be the solderpaste you are using. I know in the day when I used Alpha OA paste (WS609) it induced voids like crazy. Not all voiding is necessarily bad though, switching to Kester (at the time) greatly reduced the voiding. I am currently running AIM paste and do not experience any significant voiding.

Good Luck

Royce
***********************************************************************
Royce Taylor
Process Engineering
Suntron Corporation NEO
104 Glenn Street
Lawrence, MA 01843
(978) 747-2061 voice
(978) 747-2010 fax
[log in to unmask]
www.suntroncorp.com


-----Original Message-----
From: Yannick Brisson [mailto:[log in to unmask]]
Sent: Tuesday, January 28, 2003 9:29 AM
To: [log in to unmask]
Subject: [TN] Silly Question


Hi,

   I'm just wondering if someone could answer this silly question...we have
on a board some BGA and other discretes components, when we look at the
X-Ray picture we see that we have void (flux entrapment),  We look at our
BGAs and there are no trace of void before we pass it to the oven.  Our
finnish is a Tin Lead the surface is not flat( HASL), we check our profile
and everything is perfect.  Could our void could came from the finnish? like
this is not a flat surface could we find a void in the pad?? I know this
sound silly but I really don't see where those voids could came of.

  We didn't pass a empty board on the X-ray.


Thanks You

Yannick Brisson
============================
Technicien SMT
Technician SMT
M2S Électronique
2855, Rue de Celles 
Québec, Québec
G2C 1K7
Téléphone: (418) 842-1312 Ext: 264
Télécopie: (418) 842-0123
[log in to unmask]
============================

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------