TECHNET Archives

December 2002

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
"Brian D. Butler" <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Tue, 10 Dec 2002 10:38:22 -0700
Content-Type:
text/plain
Parts/Attachments:
text/plain (80 lines)
>Delivered-To: [log in to unmask]
>Delivered-To: [log in to unmask]
>Delivered-To: [log in to unmask]
>From: Eric Benjamins <[log in to unmask]>
>To: "Brian D. Butler" <[log in to unmask]>
>Subject: RE: [TN] Testing Labs, Southern California area?
>Date: Tue, 10 Dec 2002 09:21:18 -0800
>X-Mailer: Internet Mail Service (5.0.1460.8)
>
>Hello Brian,
>we would recommend MEFAS ( Micro Electronics Failure Analysis Service in
>Irvine (949) 699-0525.
>
>Best Regards: Eric Benjamins
>
>Microtek laboratories
>
>-----Original Message-----
>From: Brian D. Butler [mailto:[log in to unmask]]
>Sent: Tuesday, December 10, 2002 10:42 AM
>To: Eric Benjamins
>Subject: Fwd: [TN] Testing Labs, Southern California area?
>

>>Delivered-To: [log in to unmask]
>>Delivered-To: [log in to unmask]
>>Delivered-To: [log in to unmask]
>>X-SMF-Message-ID: 2C3E3B3001C41800
>>X-SMF-Hop-Count: 2
>>X-EXP32-SerialNo: 50000074, 00102145
>>X-Mailer: InterChange (Hydra) SMTP v3.61.08
>>Date:         Mon, 9 Dec 2002 16:54:00 -0800
>>Reply-To:     "TechNet E-Mail Forum." <[log in to unmask]>,
>>              Rick Thompson <[log in to unmask]>
>>Sender:       TechNet <[log in to unmask]>
>>From:         Rick Thompson <[log in to unmask]>
>>Subject: [TN] Testing Labs, Southern California area?
>>X-To:         "TechNet E-Mail Forum." <[log in to unmask]>
>>To:           [log in to unmask]
>>
>>Does anyone have a testing lab they could recommend for doing solder
>>joint/component analysis in So. California?  We've got some devices that
>are
>>'popping' off the board and it looks like some sort of intermetallic
>>fracture. I'd like to have it analyzed to be sure.
>>
>>Thanks in advance,
>>
>>Rick Thompson
>>
>>Sr. SMT Process Engineer
>>SMTEK International, Inc.
>>+1 (805) 532-2800
>>[log in to unmask]
>>
>>---------------------------------------------------
>>Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
>>To unsubscribe, send a message to [log in to unmask] with following text in
>>the BODY (NOT the subject field): SIGNOFF Technet
>>To temporarily halt or (re-start) delivery of Technet send e-mail to
>>[log in to unmask]: SET Technet NOMAIL or (MAIL)
>>To receive ONE mailing per day of all the posts: send e-mail to
>>[log in to unmask]: SET Technet Digest
>>Search the archives of previous posts at: http://listserv.ipc.org/archives
>>Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
>>information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
>>ext.5315
>>-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------

ATOM RSS1 RSS2