I sit next to guy with a Phd in the subject so I thought I'd better ask him.
His answer was typically academic - 'it depends'.
There are a number of different AR coats but his guess was it was likely to be
magnesium oxide which may be removed with nitric acid - however you'd better
check the compatibility with the substrate first.
He also observed that AR coating is generally 0.25 > 0.50 micrometers thick so
if you see a scratch it's almost certain the substrate is scratched also.
Regards,
>
> -----Original Message-----
> From: Jason W. Gregory [mailto:[log in to unmask]]
> Sent: Saturday, December 14, 2002 1:24 PM
> To: [log in to unmask]
> Subject: [TN] OTC-Sunglasses coating
>
> I have a question involving sunglasses that I thought maybe the experts
> here that work with optics lenses or the chemical gurus could answer.
>
> I have a pair of sunglasses that have gotten something on the lenses, I
> don't know what. The reflective coating has been damaged extensively. The
> company that manufactured these sunglasses has been bought by someone else
> and there is no way to get my hands on replacement lenses. These are VERY
> expensive shades, keep in mind, so I really want to fix these. What would
> be the best chemical to just go ahead and strip the remaining reflective
> coating off of these? If I can accomplish this, then would there be any way
> to recoat the reflective coating? or send them off for recoating??? Any
> help is appreciated.
>
> Thanks,
> Jason Gregory
>
> ---------------------------------------------------
> Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
> [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
> [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
> ext.5315
> -----------------------------------------------------
>
> ---------------------------------------------------
> Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
> Search the archives of previous posts at: http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
> -----------------------------------------------------
--
Eric Christison
Mechanical Engineer
STMicroelectronics
33 Pinkhill
Edinburgh
EH12 7BF
tel: +44 (0)131 336 6165
fax: +44 (0)131 336 6001
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|
|
|