Add "temperature of the solder is too high"...jk
>-----Original Message-----
>From: TechNet [mailto:[log in to unmask]] On Behalf Of Francis Sun
>Sent: Wednesday, December 11, 2002 11:00 AM
>To: [log in to unmask]
>Subject: [TN] Solder ball causes
>
>
>Hello,
>
>I would like to compile a list of what may cause solder balls
>to form after reflow for our internal consumption. Can anyone
>add to my limited knowledge on some of the causes that can
>create solder balls? My knowledge is limited and some may not
>be correct. If any are not correct please point them out. If
>there is a comprehensive list available in the public domain,
>it would be great if someone can point me in the general
>direction of where it is located.
>
>
>Some of the causes that I sort of know of: !! BE WARNED !!
>some or all
>may not be correct. :
>
>Moisture from substrate and components
>Dry solder paste
>Wet solder paste?
>Stencil aperture(s) too big
>Wrong pad geometries
>Poor mixing of solder paste
>Solder did not reach room temperatures?
>Solder paste passed shelf life?
>Environment to humidity?
>insufficient heat
>Dwell time under liqudius is too long?
>Dwell time under liqudious is too short?
>Time interval too long between solder application and reflow?
>
>Any help is appreciated.
>
>
> Happy Holidays to all
>
>Francis Sun
>MARK IV Industries
>(905) 624-3025 ext. 1235
>Fax: (905) 624-4572
>
>---------------------------------------------------
>Technet Mail List provided as a free service by IPC using
>LISTSERV 1.8e To unsubscribe, send a message to
>[log in to unmask] with following text in the BODY (NOT the
>subject field): SIGNOFF Technet To temporarily halt or
>(re-start) delivery of Technet send e-mail to
>[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE
>mailing per day of all the posts: send e-mail to
>[log in to unmask]: SET Technet Digest Search the archives of
>previous posts at: http://listserv.ipc.org/archives Please
>visit IPC web site http://www.ipc.org/html/forum.htm for
>additional information, or contact Keach Sasamori at
>[log in to unmask] or 847-509-9700 ext.5315
>-----------------------------------------------------
>
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|
|
|