MIchael,
Not sure what your black stuff is, but usually they are non-conductive :-)
You might try one of Hysol (Loctite's) glob top encapsulants for COB
applications.
From your meager detail, it is a bit hard to suggest a specific product, but
scrounge around their web site and have a look
<http://www.loctite.com/electronics/>
If you try the FP 4470, you will likely need a dam material. Others require
no dams
Steven Creswick - Gentex Corporation
-----Original Message-----
From: Mike Kuczynski [mailto:[log in to unmask]]
Sent: Monday, December 09, 2002 9:40 AM
To: [log in to unmask]
Subject: [TN] Mounting Modified BGA
I need some information in mounting a BGA asic, that has been
modified. The top is cut-off, modifications to the wirebonds to the die are
made. Then it's sealed w/ this black gunk and covered
by this yellowish film. The problem is that this black gunk is
melting and shorting out the whole die, when the BGA is being mounted on the
PCB.
Is there a different sealant (black gunk) we should be using to
close up this BGA? Could it be exceeding the temp. when mounting the BGA? Is
there another process we should look at?
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|
|
|