We are looking at using a Semtech Microbuddy and I was wondering if anyone out there has any experience with this part? My main concern is the part to pcb gap in regards to flux entrapment. The min stand off height is 0, nominal is .02mm and max is .05mm. We had wanted to use a no clean solder and flux but the customer is not interested in no clean flux residues. So, if you have used it please let me know what fluxes may have been used and also the method of cleaning. Also if you did use a cleanable flux what ionic testing results did you find.
Here is the pdf file for the part spec in case you are interested. http://semtech.com/pdf/sh3000.pdf
Thanks in advance
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
<!DOCTYPE HTML PUBLIC "-//W3C//DTD HTML 4.0 Transitional//EN">
<HTML><HEAD>
<META http-equiv=Content-Type content="text/html; charset=iso-8859-1">
<META content="MSHTML 6.00.2715.400" name=GENERATOR></HEAD>
<BODY style="MARGIN-TOP: 2px; FONT: 8pt MS Sans Serif; MARGIN-LEFT: 2px">
<DIV><FONT size=1>We are looking at using a Semtech Microbuddy and I was
wondering if anyone out there has any experience with this part? My main
concern is the part to pcb gap in regards to flux entrapment. The min
stand off height is 0, nominal is .02mm and max is .05mm. We had wanted to
use a no clean solder and flux but the customer is not interested in no clean
flux residues. So, if you have used it please let me know what fluxes may
have been used and also the method of cleaning. Also if you did use a
cleanable flux what ionic testing results did you find. </FONT></DIV>
<DIV><FONT size=1></FONT> </DIV>
<DIV><FONT size=1>Here is the pdf file for the part spec in case you are
interested. <A
href="http://semtech.com/pdf/sh3000.pdf">http://semtech.com/pdf/sh3000.pdf</A></FONT></DIV>
<DIV><FONT size=1></FONT> </DIV>
<DIV><FONT size=1>Thanks in advance</FONT></DIV></BODY></HTML>
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|
|
|