When you say .0003 plated on top of 1/2 oz. copper, you mean .0003 inches of tin-lead on top of the copper, right? Plating .0003 copper on the surface would give you less than .0003 in the holes (ignoring pulse plating which can put more in the holes than on the surface), which would be doomed to fail. They probably mean 1/2 oz. Cu foil to start, plated up 1 mil , then plated with .0003 in tin-lead, which by the way is thicker than what you'll get with HASL.
-----Original Message-----
From: Graham Collins [mailto:[log in to unmask]]
Sent: Thursday, October 17, 2002 9:52 AM
Subject: Re: [TN] how thick is ½ ounce copper
Hi Brad
Thank-you to all who answered this question, the .0006 - .0007 is more than accurate enough for my purposes, I was trying to determine the final thickness of a trace given that the PWB drawing calls for ½ ounce plus .0003 plated on top of that. I don't think I have anything that can measure to the .00091723 precision... :-)
As always, Technet folks come through. Thanks again!
regards,
Graham Collins
Process Engineer,
Northrop Grumman Canada Corporation
Halifax
(902) 873-2000 ext 6215
>>> <[log in to unmask]> 10/17/02 01:22PM >>>
There is no "simple" answer... not if I can help it.
The thickness of Metal Foil -Copper- depends on tolerance type: 10% for deposited and 5% for wrought. The nominal thickness listed in IPC-MF-150 is .68 mils. My opinion follows:
If I were producing copper foil daily, by the linear mile, it would be to my economic advantage to produce to the low side. Hence the propensity is for the copper to come in the low side of tolerance. After lamination (at laminate supplier and or PWB/PCB fabricator) the copper tendency is to reduce in thickness due to cleaning [cleaning aka etch, or if it is more palatable "micro etch"], it definitely doesn't get thicker.
It took me a while to adjust downward from .0007 to .0006 but I did, I feel it represents worse case. Different treatments and tooth of copper also factors, but my simple answer is
half ounce tends to be .0006 inch thick in the deliverable PCB. Exact measuring will probably be .00061723.
Brad
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|