My (very limited) knowledge of so-called fatigue-resistant soldersis that
they are fairly normal eutectic solder alloys, but the particle size and
shape is carefully controlled, and the paste has a number of dopants added.
The overall effect is that FRS's have a slightly lower melting point than
normal and produce very fine-grained solder joints.
My feeling about them is that they only prolong the inevitable a little -
the joints will still tend to coarsen with time and temperature, and
intermetallic layers wil also grow. It's highly debatable whether the extra
cost of this type of solder is cost effective in terms of extending solder
joint life.
There is some info on the WWW about FRS's, but not a lot.
Peter
Phillip Hinton <[log in to unmask]> 18/09/2002 10:55 AM
Sent by: TechNet <[log in to unmask]>
Please respond to "TechNet E-Mail Forum."; Please respond to Hintpwb1
To: [log in to unmask]
cc: (bcc: DUNCAN Peter/Asst Prin Engr/ST Aero/ST Group)
Subject: [TN] Theramal Fatigue Resistant Solder
All
In a presentation given by Tom Scimeca of Florida Cir Tech (time unknown)
on lead free solder he shows a graph on page 43 in which he graphs fatigue
of a "Sn63 Thermal Resistant Solder" compared to "Standard Sn63" and a
Sn/Cu with nickel (Nihon Superior Sn100C). Does anyone know what the
"(Sn63) Thermal Resistant Solder" is
Phil Hinton
520-745-1013 .
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in the
BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet
NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send
e-mail to [log in to unmask]: SET Technet Digest Search the archives of
previous posts at: http://listserv.ipc.org/archives Please visit IPC web
site http://www.ipc.org/html/forum.htm for additional information, or
contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
[This e-mail is confidential and may also be privileged. If you are not the
intended recipient, please delete it and notify us immediately; you should
not copy or use it for any purpose, nor disclose its contents to any other
person. Thank you.]
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|
|
|