Peter,
Here is my guess:
(1) if you spray from the top, you might have edge effect and height effect
(the distance from the nozzel to the coating surface).  Is the spray gun
fixed type or rotational type (multi-directional)?
(2) you should be able to confirm your thoery (charge effect) easily by
subject PWA to ionizer gas flow for few min. (ESD bentch style....you should
be able to find it in your plant).
Good luck.
                                     jk

>-----Original Message-----
>From: TechNet [mailto:[log in to unmask]]On Behalf Of
>[log in to unmask]
>Sent: Tuesday, July 23, 2002 6:43 AM
>To: [log in to unmask]
>Subject: [TN] Conformal Coating repelled by masking
>
>
>Hi, Folks,
>
>I have a theory about one phenomenon out of two that I have just witnessed,
>but seek your sage thoughts on the  matter.
>
>Our fabrication shop was spray coating an FR4 / HASL-finished board with
>Humiseal 1B31, which was masked with some very expensive Kapton tape. The
>tape is meant to be a no-static, no-residue type. We noticed that, under
>the UV inspection lamp in the spray booth, the coating appears to recede
>from the edge of the Kapton tape - at least there is a "line" 1 or 2 mm
>wide at the edge of the masking, that indicates (to me) a different
>thickness of coating in that zone compared with the rest of the board. We
>tried over-spraying the affected areas again once the initial coat had set
>a bit, but the line reappeared. It only happens where there is Kapton tape.
>
>At the same time, the coating on the solder side of the board is a nice
>shiny finish, while the component side has quite large areas that have a
>more matte, slightly "rough" appearance. I doubt there is a connection
>between the two phenomena, but you never know.
>
>My theory about coating recession from the tape is that there is a static
>charge on the Kapton tape, in spite of the "no-static" presumption, and
>that the coating particles in the spray are likewise charged from their
>passage through the spray gun. The two like charges are then repelling one
>another. I noticed that neither board nor spray gun are grounded, and think
>that they should be (comments, anyone?).
>
>My secondary theory is that the coating is reacting with the tape adhesive
>at the edge of the tape, creating a line of contamination that the coating
>doesn't stick to properly. Kapton tape is a commonly used masking material,
>though, and I haven't heard of this problem occurring with it before.
>
>I haven't come up with an explanation for the matte areas of coating on the
>component side of the board. The board had just come from the customary
>cleaning and drying that I give all boards just prior to coating.
>
>Can you come up with possible explanations and cures for what is happening
>here?
>
>MTIA
>
>Peter
>
>-------------------------------------------------------------------
>--------------
>Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
>To unsubscribe, send a message to [log in to unmask] with following text in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of Technet send e-mail
>to [log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts: send e-mail to
>[log in to unmask]: SET Technet Digest
>Search the archives of previous posts at: http://listserv.ipc.org/archives
>Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
>information, or contact Keach Sasamori at [log in to unmask] or
>847-509-9700 ext.5315
>-------------------------------------------------------------------
>--------------
>

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------

ATOM RSS1 RSS2