Mel Parrish <[log in to unmask]>
Reply To:
TechNet E-Mail Forum.
Date:
Thu, 4 Apr 2002 16:11:06 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (129 lines)
Dave and all,
From what I have seen, you are certainly correct that the plating process
contributed to the growth of whiskers.  What I do have concern for is the
inability to accelerate the growth of whiskers beyond the environment that
very closely parallels operation for electronics.  Soo how do you test for
whisker growth tendency beyond plating and waiting for four or five years to
see if it grows whiskers. Standard cycling and temperature environments only
contribute to delay whisker formation. I think that the jury is still out on
slightly elevated humidity impact. There are some very high end tests that
can compare surface tensions for compressive stresses which cause whisker
formation but I doubt if the plating shops are doing that.
I guess that I'm hoping that someone has a way to predict the tendency to
grow whiskers beyond what I've seen so far.  Our committees looking at this
haven't found one yet.
Any revelations would be appreciated.

Mel Parrish
Soldering Technology International
102 Tribble Drive
Madison, AL 35758
256 705 5530
256 705 5538 Fax
[log in to unmask]
www.solderingtech.com

-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Dave Hillman
Sent: Thursday, April 04, 2002 10:16 AM
To: [log in to unmask]
Subject: Re: [TN] Tin whiskers and immersion tin coatings


Hi Bev! We have been using immersion tin surface finish for about 1 year
and have had no issues with whisker growth. During our qualification
testing the whisker issue was a very important test matrix question and we
requested the all of the immersion tin suppliers furnish their tin whisker
data. The immersion tin chemistry suppliers (well, at least one for
certain!) appear to have successfully engineered chemistries which do not
permit whisker growth. My recommendation would be to work closely with the
pwb fabricator and/or the chemistry supplier to understand what they are
doing to eliminate whisker growth. Now if you want to really get nervous
just think about the component fabricators who are choosing to use matte
tin as a component lead finish - let's hope they have done their
homework/testing.

Dave Hillman
Rockwell Collins
[log in to unmask]




Bev Christian <[log in to unmask]>@ipc.org> on 04/02/2002 05:40:04 PM

Please respond to "TechNet E-Mail Forum." <[log in to unmask]>; Please respond
       to Bev Christian <[log in to unmask]>

Sent by:    TechNet <[log in to unmask]>


To:    [log in to unmask]
cc:

Subject:    [TN] Tin whiskers and immersion tin coatings


Technetters,
To a certain extent I am aware of the work the NEMI tin whisker task force
and various connector/component manufacturers are doing about 100% tin
coatings.  But I am still left with several questions whose answers I have
missed or questions that have not been addressed.  So... here goes - the
immersion tin coating are for SMT pads that are going to be soldered.  What
are people doing about test points? Are there stencil openings to put
solder
on these pads as well?  Or are these pads left unsoldered?  Has anyone
carried out any testing with regards to the tendency of these materials to
grow/not grow whiskers? Or do the organics in the coating completely kill
that possibility?

regards,
Bev Christian
Research in Motion

----------------------------------------------------------------------------
-----

Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send e-mail to [log in to unmask]:
SET Technet NOMAIL
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
----------------------------------------------------------------------------
-----

----------------------------------------------------------------------------
-----
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
----------------------------------------------------------------------------
-----

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------

ATOM RSS1 RSS2