Thanks for all of your response!
David, you are right, what I am looking for is ALT (accelaerated Life
Test)correlation with field application. Given our products are PC,meaning end
user environemt is not complex, is a math equation available if performing
thermal cycling or vibration to manifest the solder joint failure over the
warrenty period?
If only for the purpose of detecting solder joint failure, since it takes a
lot of efforts to make the RS vibration fixture, will thermal cycling as the
stimuli be efficient enough due to common failure mechanism--low cycle
fatigue?
Thanks again.
Mary
n Tue, 09 Apr 2002 13:00:18 -0700
David Douthit <[log in to unmask]> wrote:
>Mary Lin
>
>
>(1) Whichtest is more efficient, thermal cycling or RS Vibration? Yes!
> Why do you think it is necessary to choose?
> They are not capable of being separated if the end use has vibration
>and temperature changes.
>
>(2) how to correlate number of cycles of test (either thermal cycling or
> vibration) with service time in the field application?
> That is not the purpose of these tests!! These tests are ;
> 1. HALT is used to find the "destruction" stress limits of the product.
> 2. Hass is used to screen the products at stresses below the limits
>determined by HALT to detect
> latent defects and/or poor processes
>
>These tests are primarily used to lower warranty or infant mortality
>problems.
>What you want is sometimes referred to as ALT (Accelerated life-cycle
>Testing)
>Creating protocols that can correlate to field exposure levels is very
>complex and time consuming.
>
>Usually there is very little accurate data about the end use conditions
>available.
>The test equipment would need to be capable of synergistic combinations of
>numerous stresses.
>All in all attempting to determine the long term reliability of products is
>very problematic.
>
>David A. Douthit
>Manager
>LoCan LLC
>
>
>
>
>Mary Lin wrote:
>
>> Hello-
>>
>> As we know both thermal cycling test and RS vibration test in HALT (Highly
>> Accerlated Life Test) are effective in detecting solder joint related
>> failures.
>> Right now we are in the process of developing HASS profile, can someone help
>> me on fllowing questions?
>>
>> (1)Which test is more efficient, thermal cycling or RS Vibration?
>> (2) how to correlate number of cycles of test (either thermal cycling or
>> vibration) with service time in the field application?
>>
>> Thanks for your time.
>>
>> Mary
>> _________________________________________________________________________
>>
>> Live, laugh, and chat with friends about BMWs, Porsches, Jaguars and the new
>>MINI
>> at The World's Largest Auto Enthusiast Site
>> http://www.roadfly.org/
>>
>> ---------------------------------------------------------------------------------
>> Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
>> To unsubscribe, send a message to [log in to unmask] with following text in
>> the BODY (NOT the subject field): SIGNOFF Technet
>> To temporarily halt delivery of Technet send e-mail to [log in to unmask]: SET
>>Technet NOMAIL
>> To receive ONE mailing per day of all the posts: send e-mail to
>>[log in to unmask]: SET Technet Digest
>> Search the archives of previous posts at:
>>http://listserv.ipc.org/scripts/wa.exe?S1=technet
>> Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
>> information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
>>ext.5315
>> ---------------------------------------------------------------------------------
_________________________________________________________________________
Live, laugh, and chat with friends about BMWs, Porsches, Jaguars and the new MINI
at The World's Largest Auto Enthusiast Site
http://www.roadfly.org/
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|