DESIGNERCOUNCIL Archives

March 2002

DesignerCouncil@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Show All Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Subject:
From:
"Jack C. Olson" <[log in to unmask]>
Reply To:
(Designers Council Forum)
Date:
Mon, 4 Mar 2002 08:42:45 -0600
Content-Type:
text/plain
Parts/Attachments:
text/plain (81 lines)
I was hoping you would get an answer to this.

To me, it doesn't make sense (my knowledge
of physics is limited, to say the least), but I'm
pretty sure high voltage can arc across the
surface of a board easier than THROUGH it,
so it seems like the z-axis should be a different
value. I'm surprised to read that in para6.3

Does anyone know?
(have you gotten any private answers?)

jack





"Bundrant, Anthony" <[log in to unmask]>@IPC.ORG>
1Mar2002 11:02 AM

Please respond to "(Designers Council Forum)" <[log in to unmask]>;
      Please respond to "Bundrant, Anthony"
      <[log in to unmask]>

Sent by:  DesignerCouncil <[log in to unmask]>



To:   [log in to unmask]
cc:

Subject:  [DC] Dielectric Disconnect
Retain Until: 03/31/2002 Retention Category: G90 - Information and Reports
Caterpillar Confidential:  Green


IPC-2221, paragraph 6.3 Electrical Clearance, states: "The minimum spacing
between conductors, between conductive patterns, layer to layer conductive
spaces (z=axis), and between conductive materials (such as conductive
markings or mounting hardware) and conductors shall be in accordance with
Table 6-1, ... ."

We have a thermal plane which will see 600 volts worst case.  According to
Table 6-1, we would need roughly 20 mils of dielectric between this plane
and a routing or electrical plane layer.  Why?  The electrical strength of
polyimide from IPC-4101/42 is 29000 volts/mm (736 volts/mil).  Has anyone
had experience with this apparent disconnect between specs?

TIA,

Anthony Bundrant
Bell Helicopter Textron
Technical Resource Specialist - Electronic Packaging
817.280.8903

---------------------------------------------------------------------------------

DesignerCouncil Mail List provided as a free service by IPC using LISTSERV
1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF DesignerCouncil.
To set a vacation stop for delivery of DesignerCouncil send: SET
DesignerCouncil NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
---------------------------------------------------------------------------------

---------------------------------------------------------------------------------
DesignerCouncil Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF DesignerCouncil.
To set a vacation stop for delivery of DesignerCouncil send: SET DesignerCouncil NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------

ATOM RSS1 RSS2