Mike
You would be better to go with a conventional coating. UV is not ideal for
3D objects - works great in 2D, cos you don't have to bend light! :-)
I cannot remember what the operating environment was for your circuit - if
you would care to repeat, I can recommend something - however, I am sure
that a one part AR or UR coating from a reliable supplier will give you the
best overall results - process and operating environment.
Regards, Graham Naisbitt
[log in to unmask]
www.concoat.co.uk <http://www.concoat.co.uk>
For instant access to Product Data Sheets register on the Tech-Shot area of
http:// www.concoat.co.uk <http://www.concoat.co.uk>
Concoat Limited
Alasan House, Albany Park
CAMBERLEY GU16 7PH UK
Phone: +44 (0)1276 691100
Fax: +44 (0)1276 691227
Mobile: +44 (0)79 6858 2121
-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Mike Manwell
Sent: Thursday, December 06, 2001 02:41
To: [log in to unmask]
Subject: [TN] 2 Conformal Coating ?'s
Hello,
Thanks in advance if you have taken the time to read this!
#1- Im trying different materials in a spray application. Both are cured
using UV. One material does a "secondary cure" w/ moisture. This is cool
because after 100 hours after UV cure, all material is fully cured.
The other material Im trying uses HEAT for a secondary cure, or, if
shodowed during UV cure, the material wont cure and never will. Obviously I
dont want the stuff dripping or running anywhere, but being new to this
wonderful process, just dont feel good about leaving uncured material on a
product for it's entire life. Iv been told that you can "test" the product
to see if the uncured material is causing a problem but Im not sure what
type of test that would consist of. Any insight?
#2- Has anyone out there ever installed refelctive metal plates in their UV
oven to limit shadowing?
Thanks so much,
Mike Manwell
----------------------------------------------------------------------------
-----
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET
Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases >
E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
----------------------------------------------------------------------------
-----
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|
|
|